Related papers: Nonlinear current-voltage behavior and electricall…
Microstructure properties, phase transitions, and charge ordering in the LuFe2O4 materials have been extensively investigated by means of transmission electron microscopy (TEM). The (001) twins as a common defect frequently appear in the…
The transmission electron microscopy observations of the charge ordering (CO) which governs the electronic polarization in LuFe2O4-x clearly show the presence of a remarkable phase separation at low temperatures. Two CO ground states are…
The structural features of the charge ordering states in LuFe2O4 are characterized by in-situ cooling TEM observations from 300K down to 20K. Two distinctive structural modulations, a major q1= (1/3, 1/3, 2) and a weak q2=q1/10 + (0, 0,…
A colossal electroresistance effect is observed around room temperature in a transition metal oxide LuFe2O4. The measurements of resistance under various applied voltages as well as the highly nonlinear current-voltage characteristics…
Neutron diffraction measurements on multiferroic LuFe2O4 show changes in the antiferromagnetic (AFM) structure characterized by wavevector q = (1/3 1/3 1/2) as a function of electric field cooling procedures. The increase of intensity from…
X-ray scattering by multiferroic LuFe2O4 is reported. Below 320 K, superstructure reflections indicate an incommensurate charge order with propagation close to (1/3,1/3,3/2). The corresponding charge configuration, also found by electronic…
Non-linear conduction in a single crystal of charge-ordered Pr$_{0.63}$Ca$_{0.37}$MnO$_{3}$ has been investigated in an applied magnetic field. In zero field, the non-linear conduction, which starts at T$<$T$_{CO}$ can give rise to a region…
We present the refinement of the crystal structure of charge-ordered LuFe2O4, based on single-crystal x-ray diffraction data. The arrangement of the different Fe-valence states, determined with bond-valence-sum analysis, corresponds to a…
The crystal structure of Fe3O4 below the 122 K Verwey transition has been refined using high-resolution X-ray and neutron powder diffraction data. The refinements give direct evidence for charge ordering (CO) over four independent…
Hexagonal LuFe2O4 is a promising charge-order (CO) driven multiferroic material with high charge and spin ordering temperatures. The coexisting charge and spin orders on Fe3+/Fe2+ sites result in novel magnetoelectric behaviors, but the…
We performed elastic neutron scattering measurements on the charge- and magnetically-ordered multiferroic material LuFe(2)O(4). An external electric field along the [001] direction with strength up to 20 kV/cm applied at low temperature…
LuFe2O4 often is considered as a prototypical multiferroic with polar order arising from the electronic degrees of freedom only ("electronic ferroelectricity"). In the present work, we check the intrinsic nature of the dielectric response…
We show results of broadband dielectric measurements on the charge ordered, proposed to be mul- tiferroic material LuFe2O4. The temperature and frequency dependence of the complex permittivity as investigated for temperatures above and…
Electronic ferroelectricity from charge ordering (CO) is currently a significant issue that has been extensively investigated in the charge/spin frustrated LuFe2O4 system. Chemical substitution and structural layer intercalation have been…
A current-controlled negative differential resistance has been revealed in the I-V characteristics of single crystal La$_{2}$CuO$_{4+\delta}$ in the low temperature region. The non-linear behavior of conductivity is accompanied by a…
The reflectivity of a large LuFe(2)O(4) single crystal has been measured with the radiation field either perpendicular or parallel to the c axis of its rhombohedral structure, from 10 to 500K, and from 7 to 16000 cm-1. The transition…
Single crystals of LaFeAsO were successfully grown out of KI flux. Temperature dependent electrical resistivity was measured with current flow along the basal plane, \rho_perpend(T), as well as with current flow along the crystallographic…
Femtosecond time-resolved second harmonic generation (SHG) measurements were performed at room temperature on a single crystal of LuFe2O4, which has recently attracted attention as an electronic ferroelectric material in which polarization…
We report on electronic transport measurements in $La_2NiO_{4.14}$. Non-Ohmic and hysteretic $V(I)$ curves are measured for $T \lesssim$ 220 $K$. Large and non Gaussian resistance fluctuations can be observed, with strong cooling rate…
Neutron diffraction is used to probe the (H,T) phase diagram of magneto-electric (ME) LiNiPO4 for magnetic fields along the c-axis. At zero field the Ni spins order in two antiferromagnetic phases. One has commensurate (C) structures and…