The linear magnetoelectric effect was measured in 500 nm Cr2O3 films grown by rf sputtering on Al2O3 substrates between top and bottom thin film Pt electrodes. Magnetoelectric susceptibility was measured directly by applying an AC electric…
The transverse magnetoresistance of thin films of the Diluted Magnetic Semiconductor Zn$_{1-x}$Co$_{x}$O:Al on glass was studied for temperatures in the range of 5 to 100 K. Measurements were made on thin films grown by rf magnetron…
The periodic response of magnetoresistance to an externally tunable parameter, such as magnetic field or chemical composition, in the bulk or an artificially designed material has been exploited for technological applications as well as to…
Mn$_{3-x}$Ga (x = 0.1, 0.4, 0.7) thin films on MgO and SrTiO$_3$ substrates were investigated with magnetic anisotropy perpendicular to the film plane. An anomalous Hall-effect was observed for the tetragonal distorted lattice in the…
We report magnetostatic measurements for granulated films (CoFeB)$_{x}$-(SiO$_{2}$)$_{1-x}$ with fabrication induced intraplanar anisotropy. The measurements have been performed in the film plane in the wide temperature interval…
This letter reports our experimental results on magnetic-field-induced aftereffects in solution derived Bi4Fe2TiO12 film, in which e' decreases as much as 600 times after treated in a 5T magnetic field as that of the pristine one. The…
We fabricated Pb(Zr0.52Ti0.48)O3-NiFe2O4 composite films consisting of randomly dispersed NiFe2O4 nanoparticles in the Pb(Zr0.52Ti0.48)O3 matrix. The structural analysis revealed that the crystal axes of the NiFe2O4 nanoparticles are…
We report the magnetoresistance and nonlinear Hall effect studies over a wide temperature range in pulsed laser deposited Ni0.07Zn0.93O thin film. Negative and positive contributions to magnetoresistance at high and low temperatures have…
The magneto-transport properties of nanocomposite C:Co (15 and 40 at.% Co) thin films are investigated. The films were grown by ion beam co-sputtering on thermally oxidized silicon substrates in the temperature range from 200 to 500 degC.…
Anomalous Hall effect (AHE) of a ferromagnetic semiconductor anatase \cotio thin film is studied from 10K to 300K. Magnetic field dependence of anomalous Hall resistance is coincident with that of magnetization, while the anomalous Hall…
The resistivity, temperature, and magnetic field dependence of the anomalous Hall effect in a series of metallic Ga1-xMnxAs thin films with 0.015=<x=<0.08 is presented. A quadratic dependence of the anomalous Hall resistance on the…
We report the observation of anomalous Hall effect in Mn$_3$Sn polycrystalline thin films deposited on Pt coated Al$_2$O$_3$ substrate with a large anomalous Hall conductivity of 65($\Omega$cm)$^{-1}$ at 3K. The Hall and magnetic…
Non-monotonic dependence of anomalous Hall resistivity on temperature and magnetization, including a sign change, was observed in Fe/Gd bilayers. To understand the intriguing observations, we fabricated the Fe/Gd bilayers and single layers…
The magnetic properties of MnAs epilayers have been investigated for two different substrate orientations: GaAs(100) and GaAs(111). We have analyzed the magnetization reversal under magnetic field at low temperatures, determining the…
We demonstrate room temperature ferroelectricity in the epitaxial thin films of magnetoelectric GaFeO3. Piezo-force measurements show a 180o phase shift of piezoresponse upon switching the electric field indicating nanoscale…
Earlier a magnetic anisotropy for magnetic impurities nearby the surface of non-magnetic host was proposed in order to explain the size dependence of the Kondo effect in dilute magnetic alloys. Recently Giordano has measured the…
The Hall resistivity, magnetoresistance, and magnetization of La_{1-x}Ca_{x}CoO_{3} epitaxial films with x between 0.25 and 0.4 grown on lanthanum aluminate were measured in fields up to 7 T. The x=1/3 film, shows a reentrant metal…
Good quality and fine grain Bi6Fe2Ti3O18 magnetic ferroelectric films with single-phase layered perovskite structure have been successfully prepared via metal organic decomposition (MOD) method. Results of low-temperature magnetocapacitance…
Magnetite epitaxial thin films have been prepared by pulsed laser deposition at 340 C on MgO and Si substrates. One key result is that the thin film properties are almost identical to the properties of bulk material. For 40 - 50 nm thick…
We prepared high epitaxial thin films of the compound Sr_2FeMoO_6 with narrow rocking curves by pulsed laser deposition. The diagonal and nondiagonal elements of the resistivity tensor were investigated at temperatures from 4 K up to room…