Related papers: Influence of Mg Deficiency on the Superconductivit…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
A Hybrid Physical-Chemical Vapour Deposition (HPCVD) system consisting of separately controlled Mg-source heater and substrate heater is used to grow MgB2 thin films and thick films at various temperatures. We are able to grow…
The effects of high-temperature vacuum-annealing induced Mg deficiency in MgB2 single crystals grown under high pressure were investigated. As the annealing temperature was increased from 800 to 975 C, the average Mg content in the MgB2…
Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in…
Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…
We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…
We have studied the effect of deposition rate and layer thickness on the properties of epitaxial MgB2 thin films grown by hybrid physical-chemical vapor deposition on 4H-SiC substrates. The MgB2 film deposition rate depends linearly on the…
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…
We have investigated the thermodynamic and kinetic barriers involved in the synthesis of MgB2 films. This work refines our initial conjectures predicting optimal MgB2 thin film growth conditions as a consequence of the unusually large…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
The in situ annealing conditions of pulsed laser deposited MgB2 films were studied. The precursor films were deposited at 250 C from a stoichiometric MgB2 target in a 120mTorr Ar atmosphere. The films were then in situ annealed at a…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
The effect of damage induced by 2-MeV alpha particles, followed by annealing, on the critical temperature (Tc), resistivity, and upper critical field (Hc2), of three MgB2 films made by different deposition processes has been studied. Damage…
We have grown MgB2 films in a postannealing process. Precursors were prepared on Al2O3(0001) substrates by codeposition of Mg and MgB2 using pulsed laser deposition technique. Superconducting MgB2 thin films were obtained via an ex situ…
The in-situ growth of superconducting MgB2 thin films was examined from various perspectives. The paper discusses (1) growth temperature, (2) the effect of excess Mg, (3) the effect of residual gas during growth, (4) the effect of in-situ…
Superconducting thin films of MgB2 were deposited by Pulsed Laser Deposition on magnesium oxide and sapphire substrates. Samples grown at 450C in an argon buffer pressure of about 10-2 mbar by using a magnesium enriched target resulted to…
The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron…
MgB2 thin films were deposited on SiC buffered Si substrates by sequential electron beam evaporation of B-Mg bilayer followed by in-situ annealing. The application of a SiC buffer layer enables the maximum annealing temperature of 830 C.…
Superconducting thin films have been prepared in a two-step in-situ process, using the Mg-B plasma generated by pulsed laser ablation. The target was composed of a mixture of Mg and MgB2 powders to compensate for the volatility of Mg and…
We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…