Unveiling point defects concentration in transition metal oxide thin films is essential to understand and eventually control their functional properties, employed in an increasing number of applications and devices. Despite this unquestionable interest, there is a lack of available experimental techniques able to estimate the defect chemistry and equilibrium constants in such oxides at intermediate-to-low temperatures. In this study, the defect chemistry of a relevant material such as La1-xSrxFeO3-d (LSF) with (x = 0.2, 0.4 and 0.5 (LSF20, LSF40 and LSF50 respectively) is obtained by using a novel in situ spectroscopic ellipsometry approach applied to thin films. Through this technique, the concentration of holes in LSF is correlated to measured optical properties and its evolution with temperature and oxygen partial pressure is determined. In this way, a systematic description of defect chemistry in LSF thin films in the temperature range from 350dC to 500dC is obtained for the first time, which represents a step forward in the understanding of LSF20, LSF40 and LSF50 for emerging low temperature applications.
@article{arxiv.2105.13039,
title = {Pushing the Study of Point Defects in Thin Film Ferrites to Low Temperatures Using In Situ Ellipsometry},
author = {Yunqing Tang and Francesco Chiabrera and Alex Morata and Inigo Garbayo and Nerea Alayo and Albert Tarancon},
journal= {arXiv preprint arXiv:2105.13039},
year = {2021}
}