The ability to synthesis well-ordered two-dimensional materials under ultra-high vacuum and directly characterize them by other techniques in-situ can greatly advance our current understanding on their physical and chemical properties. In this paper, we demonstrate that iso-oriented {\alpha}-MoO3 films with as low as single monolayer thickness can be reproducibly grown on SrTiO3(001) (STO) substrates by molecular beam epitaxy ( (010)MoO3 || (001)STO, [100]MoO3 || [100]STO or [010]STO) through a self-limiting process. While one in-plane lattice parameter of the MoO3 is very close to that of the SrTiO3 (aMoO3 = 3.96 {\AA}, aSTO = 3.905 {\AA}), the lattice mismatch along other direction is large (~5%, cMoO3 = 3.70 {\AA}), which leads to relaxation as clearly observed from the splitting of streaks in reflection high-energy electron diffraction (RHEED) patterns. A narrow range in the growth temperature is found to be optimal for the growth of monolayer {\alpha}-MoO3 films. Increasing deposition time will not lead to further increase in thickness, which is explained by a balance between deposition and thermal desorption due to the weak van der Waals force between {\alpha}-MoO3 layers. Lowering growth temperature after the initial iso-oriented {\alpha}-MoO3 monolayer leads to thicker {\alpha}-MoO3(010) films with excellent crystallinity.
@article{arxiv.1511.02255,
title = {Iso-oriented monolayer {\alpha}-MoO3(010) films epitaxially grown on SrTiO3(001)},
author = {Yingge Du and Guoqiang Li and Erik W. Peterson and Jing Zhou and Xin Zhang and Rentao Mu and Zdenek Dohnálek and Mark Bowden and Igor Lyubinetsky and Scott A. Chambers},
journal= {arXiv preprint arXiv:1511.02255},
year = {2016}
}
Comments
One supporting figure is attached at the end of the manuscript