Related papers: In-plane optical response of Bi2Sr2CuO6

We measured the reflectivity of the multifold semimetal RhSi in a frequency range from 80 to 20000 cm$^{-1}$ (10 meV - 2.5 eV) at temperatures down to 10 K. The optical conductivity, calculated from the reflectivity, is dominated by the…

Infrared reflectivity measurements, using p-polarized light at a grazing angle of incidence, show an increased sensitivity to the optical conductivity of highly reflecting superconducting materials. We demonstrate that when this measurement…

We report on the ab-plane reflectance of the high temperature superconductor Bi2Sr2CaCu2O8+d (Bi-2212). Samples spanning the doping range from under doped with Tc = 67 K(UD), to optimally doped with Tc = 96 K (OPT), to over doped with Tc =…

Superconducting Pr$_2$CuO$_x$, $x\simeq 4$ (PCO) films with $T^\prime$ structure and a $T_c$ of 27 K have been investigated by various optical methods in a wide frequency (7 - 55000 cm$^{-1}$) and temperature (2 to 300 K) range. The optical…

Systematic microwave surface impedance measurements of YBCO single crystals grown in $BaZrO_3$ crucibles reveal new properties that are not directly seen in similar measurements of other YBCO samples. Two key observations obtained from…

We have measured the ab-plane resistivity of La$_{2-x}$Sr$_x$CuO$_4$ single crystals with small Sr content (x=0.052 $\div$ 0.075) between 4.2 and 300 K by using the AC Van der Pauw technique. As recently suggested by Ichikawa et al., the…

The optical conductivity of single crystals of Na_xCoO_2 for $x$ = 0.57 is first reported between 295 and 30 K. In the far infrared, an "anomalous Drude" analysis leads to a carrier effective mass of 5 electron masses. That this high value…

The a-axis optical properties of a detwinned single crystal of YBa_2Cu_3O_6.50 in the ortho II phase (Ortho II Y123, T_c= 59 K) were determined from reflectance data over a wide frequency range (70 - 42 000 cm^-1) for nine temperature…

The optical properties of the superconducting single crystal Rb$_{0.8}$Fe$_{1.68}$Se$_2$ with $T_{c}$ $\simeq$ 31 K have been measured over a wide frequency range in the $ab$ plane. We found that the optical conductivity is dominated by a…

The time-averaged and low--frequency noise transport properties were investigated in the vicinity of the superconductor--insulator transition for a Bi$_2$Sr$_{2-x}$La$_{x}$CuO$_{6+\delta}$ ($x=0.3$) thin film. The results are consistent…

The ab-plane reflectivity of (Y{1-x}Prx)Ba2Cu3O7 thin films was measured in the 30-30000 cm-1 range for samples with x = 0 (Tc = 90 K), x = 0.4 (Tc = 35 K) and x = 0.5 (Tc = 19 K) as a function of temperature in the normal state. The…

Infrared reflection and transmission as a function of temperature have been measured on single crystals of Cu$_{3}$Bi(SeO$_{3}$)$_{2}$O$_{2}$Cl. The complex dielectric function and optical properties along all three principal axes of the…

The out-of-plane dielectric constant of the parent insulator of the high-temperature superconductor Bi_2Sr_2(Dy,Er)Cu_2O_8 was measured and analysed from 80 to 300 K in the frequency range of 10^6-10^9 Hz. All the samples were found to show…

The oxygen dopant concentration dependence of the "quasiparticle" feature at 600-750 cm-1 of the infrared spectrum of Bi2Sr2CaCu2O8+delta (BSCCO), lying near and above the top of the host phonon spectrum at 600 cm-1, is strongly correlated…

We report on field-induced variations of the microwave surface resistance at 9.6 GHz of Ba(0.6)K(0.4)BiO(3) crystals. Energy losses have been investigated as a function of the static magnetic field in the range of temperatures 4.2 K - Tc.…

We report the complex dielectric function of high-quality nearly-stoichiometric Rb2Fe4Se5 (RFS) single crystals with Tc=32 K determined by wide-band spectroscopic ellipsometry and time-domain transmission spectroscopy in the spectral range…

Most of the novel superconductors are uniaxial crystals, with metallic planes ($ab$) orthogonal to an insulating axis ($c$). Far-infrared measurements of the reflectivity $R_{ab} (\omega)$ provide valuable information on their low-energy…

We present results of reflectivity measurements with E parallel to c and E perpendicular to c on NdBa2Cu3Ox (Nd123) single crystals close to full oxygen doping. Along the c-axis the optical conductivity shows a well developed absorption…

We report optical (6 meV - 4 eV) properties of a boride superconductor ZrB$_{12}$ ($T_c$ = 6 K) in the normal state from 20 to 300 K measured on high-quality single crystals by a combination of reflectivity and ellipsometry. The Drude…

A single crystal of isovalently substituted Ba(Fe$_{1-x}$Ru$_{x}$)$_2$As$_2$ ($x=0.24$) was sequentially irradiated with 2.5 MeV electrons up to a maximum dose of $2.1 \times 10^{19}$ electrons/cm^2. The electrical resistivity was measured…