Fe-sheathed MgB2 tapes were prepared through the in situ powder-in-tube technique by 5 at.% ZrSi2, ZrB2 and WSi2 doping, respectively. The doping effect of these compounds on the microstructure and superconducting properties of MgB2 tapes…
MgB2/Fe tapes with 2.5-15 at.% ZrB2 additions were prepared through the in situ powder-in-tube method. Compared to the pure tape, a significant improvement in the in-field critical current density Jc was observed, most notably for 10 at.%…
Nanocarbon-doped Fe-sheathed MgB2 tapes with different doping levels were prepared by the in situ powder-in-tube method. Compared to the undoped tapes, Jc for all the C-doped samples was enhanced by more than an order of magnitude in…
The nano-SiC doped MgB2/Fe wires were fabricated using a powder-in-tube method and an in-situ reaction process. The depression of Tc with increasing SiC doping level remained rather small due to the counterbalanced effect of Si and C…
MoSi2 doped MgB2 tapes with different doping levels were prepared through the in-situ powder-in-tube method using Fe as the sheath material. Effect of MoSi2 doping on the MgB2/Fe tapes was investigated. It is found that the highest JC value…
We report on significant flux pinning enhancement in MgB2/Fe tapes that has been easily obtained by a simple and cheap route using acetone as both an efficient ball-milling medium and liquid additive through the in situ method. Results…
Fe-clad BaxK1-xFe2As2 superconducting tapes were fabricated by the ex situ powder-in-tube method combined with a short high-temperature annealing technique. The effect of annealing time and different dopants on the transport properties of…
The effect of nano-C doping on the microstructure and superconducting properties of Fe-sheathed MgB2 tapes prepared through the in-situ powder-in-tube method was studied. Heat treatment was performed at a low temperature of 650C for 1 h.…
A review of current developments in the study of chemical doping effect on the superconducting properties of MgB2 wires and tapes is presented, based on the known literature data and our own results. The critical current density of MgB2 can…
We report on the superconducting performance of the ex-situ SiC doped MgB2 monofilamentary tapes. Polycrystalline powders of MgB2 doped with 5 and 10 wt% SiC were synthesized by conventional solid-state reaction route and characterized for…
The effect of the quality of starting powders on the microstructure and superconducting properties of in-situ processed Fe-sheathed MgB2 tapes has been investigated. Three different types of commercial atomized spherical magnesium powder…
Doping of MgB2 by nano-SiC and its potential for improvement of flux pinning was studied for MgB2-x(SiC)x/2 with x = 0, 0.2 and 0.3 and a 10wt% nano-SiC doped MgB2 samples. Co-substitution of B by Si and C counterbalanced the effects of…
We investigated the effect of nanoscale-C doping on the critical current density Jc and irreversibility field Birr of Fe-sheathed MgB2 tapes prepared by the in-situ powder-in-tube method. The tapes were heat treated at 600-950C for 1 h.…
MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density…
A significant enhancement of Jc and Hirr in MgB2 tapes has been achieved by the in situ powder-in-tube method utilizing hollow carbon spheres (HCS) as dopants. At 4.2 K, the transport Jc for the 850C sintered samples reached 3.1x10^4, and…
We report on the preparation of dense monofilamentary MgB2/Ni and MgB2/Fe tapes with high critical current densities. In annealed MgB2/Ni tapes, we obtained transport critical current densities as high as 2.3*105 A/cm2 at 4.2 K and 1.5 T,…
Fe/MgB2 tapes have been prepared starting with pre-reacted binary MgB2 powders. As shown by resistive and inductive measurements, the reduction of particle size to a few microns by ball milling has little influence on Bc2, while the…
We report the synthesis and characterization of graphite (C) doped MgB2-xCx (x = 0.0, 0.1, 0.2 and 0.3) samples. The crystal structure and microstructural characterization have been investigated by x-ray diffractometer and transmission…
The effect of doping MgB2 with carbon nanotubes on transition temperature, lattice parameters, critical current density and flux pinning was studied for MgB2-xCx with x = 0, 0.05, 0.1, 0.2 and 0.3. The carbon substitution for B was found to…
The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing…