MgB2 wires and tapes suffer from a limitation of the transport current densities, especially at low field, due to an unsufficient thermal stabilization caused by hot spots from a non-homogeneous microstructure, the presence of secondary…
In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different…
MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density…
The superconducting properties of copper-sheathed MgB2 wires fabricated by conventional powder-in-tube techniques and the in-situ reaction procedure are analysed. The influence of the processing conditions and initial (1+x)Mg + 2B (x = 0,…
Multifilamentary MgB2/Fe wires and tapes with high transport critical current densities have been fabricated using a straightforward powder-in-tube (PIT) process. After annealing, we measured transport jc values up to 1.1 * 105 A/cm2 at 4.2…
We have fabricated a series of iron-sheathed superconducting wires prepared by the powder-in-tube technique from (MgB_2)_{1-x}:(Mg+2B)_x initial powder mixtures taken with different proportions, so that x varies from 0 to 1. It turned out…
The Powder-In-Tube process has been employed to fabricate tape-like conductors with a strong metallic sheath and based on the newly discovered MgB2 superconducting phase. Long superconducting tapes have been prepared by packing reacted MgB2…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
We report dc transport and magnetization measurements of Jc in MgB2 wires fabricated by the powder-in-tube method, using commercial MgB2 powder with 5 %at Mg powder added as an additional source of magnesium, and stainless steel as sheath…
An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter…
The powder in tube method has been used to fabricate Ag and Cu clad MgB2 wires using an in-situ reaction method. The effects of short time sintering on the critical current densities of Ag and Cu clad MgB2 wires were studied. All the…
The microstructures of MgB2 wires prepared by the powder-in-tube technique and subsequent hot isostatic pressing were investigated using transmission electron microscopy. Large amount of crystalline defects including small angle twisting,…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
Mono- and multifilamentary MgB2/Fe tapes and wires with high transport critical current densities have been prepared using the powder-in-tube (PIT) process. The fabrication details are described. The effect of powder grain sizes and…
The nano-SiC doped MgB2/Fe wires were fabricated using a powder-in-tube method and an in-situ reaction process. The depression of Tc with increasing SiC doping level remained rather small due to the counterbalanced effect of Si and C…
Recent advances in MgB2 conductors are leading to a new level of performance. Based on the use of proper powders, proper chemistry, and an architecture which incorporates internal Mg diffusion (IMD), a dense MgB2 structure with not only a…
The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…
We have fabricated a series of ex situ copper sheathed powder-in-tube MgB2 wires with 20% by volume Ag, Pb, In, and Ga metal added to the MgB2 powder. We find the transport critical current of these wires increases significantly with the…
We succeeded in the fabrication of high-Jc MgB2/Fe wires applying the internal Mg diffusion (IMD) process with pure Mg core and SiC addition. A pure Mg rod with 2 mm diameter was placed at the center of a Fe tube, and the space between Mg…
MgB2 monofilamentary nickel-sheated tapes and wires were fabricated by means of the ex-situ powder-in-tube method using either high-energy ball milled and low temperature synthesized powders. All sample were sintered at 920 C in Ar flow.…