Related papers: Drastic improvement of surface structure and curre…

Thin films of the superconductor YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) were modified by low-energy light-ion irradiation employing collimated or focused He$^+$ beams, and the long-term stability of irradiation-induced defects was investigated.…

YBCO films were successfully prepared on biaxially textured Ag{110}<211> substrates by using pulsed laser deposition. X-ray diffraction results showed that the degree of preferential orientation of Ag{110}<211> substrates varied with…

YBaCuO nanowires were reproducibly fabricated down to widths of 50 nm. A Au/Ti cap layer on YBCO yielded high electrical performance up to temperatures above 80 K in single nanowires. Critical current density of tens of MA/cm2 at T = 4.2 K…

We have grown untwinned YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on (110) MgO substrates that were pre-annealed at high temperature in oxygen atmosphere. The annealing results in surface reconstruction with shallow facets, which induce the…

Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of…

Bi2Sr2Ca1Cu2O8+d (Bi-2212) thin films with thicknesses less than 50 nm (<20 unit cells) are grown by pulsed laser deposition (PLD) onto (001) LaAlO3 (LAO) single crystal substrates. Phase-pure and smooth c-axis oriented Bi-2212 films with…

Spatially-resolved studies of a YBaCuO thin film bridge using electron probe microanalysis (EPMA), low-temperature scanning electron microscopy (LTSEM), and magneto-optical flux visualization (MO) have been carried out. Variations in…

The dynamics of transient current distributions in superconducting YBCO thin films were investigated during and immediately following an external field ramp, using high-speed (real-time) Magneto-Optical Imaging and calculation of dynamic…

We report measurements of the thermoelectric power and electrical resistivity of superlattices composed of the high-temperature superconductor YBa2Cu3O(7-delta) (YBCO) and the metallic ferromagnet La(2/3)Ca(1/3)MnO3 (LCMO) with individual…

We report a large persistent photoconductivity (PPC) in oxygen reduced PLD grown YBa2Cu3O7-{\delta}/La2/3Ca1/3MnO3-y (YBCO/LCMO) superlattices scaling with the oxygen deficiency and being similar to that observed in single layer…

We present harmonic generation measurements of the intrinsic nonlinear current density $j_2$ of YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films at temperatures close the $T_c$. Experiments on a range of different quality samples allow us to…

We have measured the penetration depth of overdoped Y0.9Ca0.1Ba2Cu3O7-delta (Ca-YBCO) thin films using two different methods. The change of the penetration depth as a function of temperature has been measured using the parallel plate…

It is known that solid-state reaction in high-pressure oxygen can stabilize high-oxidation phases of Y-Ba-Cu-O superconductors in powder form. We extend this superoxygenation concept of synthesis to thin films which, due to their large…

Ba(Fe1-xCox)2As2 is the most tunable of the Fe-based superconductors (FBS) in terms of acceptance of high densities of self-assembled and artificially introduced pinning centres which are effective in significantly increasing the critical…

We have studied the local critical current density, jc, in the superconductor thin film of bilayer structures consisting of YBa2Cu3O7 and the ferromagnets La2/3Ca1/3MnO3 and SrRuO3, respectively, by means of quantitative magneto-optics. A…

Local surface conductivity properties and surface degradation of c-axis oriented YBa2Cu3O6+x (YBCO) thin films were studied by Scanning Spreading Resistance Microscopy (SSRM). For the surface degradation studies, the YBCO surface was…

Freestanding GdBa2Cu3O7 (GdBCO) superconducting thin films were fabricated using a water-soluble Sr3Al2O6 (SAO) sacrificial layer in combination with thermal release tape. An amorphous Al2O3 capping layer was introduced to suppress crack…

We have studied nodal tunneling into YBa2Cu3O7-x (YBCO) films under magnetic fields. The films' orientation was such that the CuO2 planes were perpendicular to the surface with the a and b axis at 450 form the normal. The magnetic field was…

We examine the effect of CuO intergrowths on the superconductivity in epitaxial La_{2/3}Ca_{1/3}MnO_3/YBa_2Cu_3O_{7-\delta} (LCMO/YBCO) thin-film heterostructures. Scanning transmission electron microscopy on bilayer LCMO/YBCO thin films…

We observe a strong reduction of the field induced thin film surface resistance measured at high microwave frequency ($\nu=$47.7 GHz) in YBa$_{2}$Cu$_{3}$O$_{7-\delta}$ thin films grown on SrTiO$_3$ substrates, as a consequence of the…