Related papers: Synthesis of Mg(B$_{1-x}$C$_x$)$_2$ Powders
Measurements of the penetration depth $\lambda (T,H)$ in the presence of a DC magnetic field were performed in $MgB_2$ wires. In as-prepared wires $\lambda (T,H<130 Oe)$ shows a strong diamagnetic downturn below $\approx 10 K$. A DC…
Magnetic ions (Mn) were substituted in MgB_2 single crystals resulting in a strong pair-breaking effect. The superconducting transition temperature, T_c, in Mg_{1-x}Mn_xB_2 has been found to be rapidly suppressed at an initial rate of 10…
Detailed magneto-transport data on dense wires of $MgB_2$ are reported for applied magnetic fields up to 18 T. The temperature and field dependencies of the electrical resistivity are consistent with $MgB_2$ behaving like a simple metal and…
Single crystals of MgB2 have been grown at high pressure via the peritectic decomposition of MgNB9. The crystals are of a size up to 1.5x0.9x0.2 mm3 with a weight up to 0.23 mg, and typically have transition temperatures between 37 and 39…
The accurate charge density of MgB2 was observed at room temperature(R.T.) and 15K by the MEM(Maximum Entropy Method)/Rietveld analysis using synchrotron radiation powder data. The obtained charge density clearly revealed the covalent…
In the present study, we report a systematic study of doping/ admixing of carbon nanotubes (CNTs) in different concentrations in MgB2. The composite material corresponding to MgB2+ x at.%CNTs (35 at.% > x > 0 at.%) have been prepared by…
W-B-C films were deposited on Si(100) substrates held at elevated temperature by reactive sputtering from a W target in Kr/trimethylboron (TMB) plasmas. Quantitative analysis by X-ray photoelectron spectroscopy (XPS) shows that the films…
By devising a novel framework, we present a comprehensive theoretical study of solubilities of alkali (Li, Na, K, Rb, Cs) and alkaline earth (Be, Ca, Sr, Ba) metals in the he boron-rich Mg-B system. The study is based on first-principle…
The thermal stability of MgB2 has been studied experimentally to determine the role of thermodynamic and kinetic barriers in the decomposition process. The MgB2 decomposition rate approaches one monolayer per second at 650 C and has an…
The effects of high-temperature vacuum-annealing induced Mg deficiency in MgB2 single crystals grown under high pressure were investigated. As the annealing temperature was increased from 800 to 975 C, the average Mg content in the MgB2…
Understanding of recently reported putative close-to-room-temperature superconductivity in C-S-H compounds at 267 GPa demands reproducible synthesis protocol as well as knowledge of its structure and composition. We synthesized C-S-H…
In this study, Si and C were incorporated into polycrystalline MgB2 via in situ reaction of Mg and B with either SiC or with separate Si and C (Si+C). The electrical transport and magnetic properties of the two series of samples were…
Two new methods to produce nanopowders of B12P2 boron subphosphide by self-propagating high-temperature synthesis have been proposed. Bulk polycrystalline B12P2 with microhardness of HV = 35(3) GPa and stability in air up to 1300 K has been…
A commercial stainless steel tube was employed to synthesize MgB2. The specimen was prepared by a stoichiometric mixture of Mg and B. The specimen that had been enveloped in the commercial stainless steel tube was synthesized for 2 hours at…
Studies of the behaviour of solids at ultra-high pressures, those beyond 200 GPa, contribute to our fundamental understanding of materials properties and allow an insight into the processes happening at such extreme conditions relevant for…
0.5 to 5.0 wt.% Dy2O3 was in-situ reacted with Mg + B to form pinned MgB2. While Tc remained largely unchanged, Jc was strongly enhanced. The best sample (only 0.5 wt.% Dy2O3) had a Jc of 6.5 x 10^5 A/cm^2 at 6K, 1T and 3.5 x 10^5 A/cm^2 at…
Nb3Sn was prepared by milling Nb and Sn powder mixtures followed by limited reactions to restrict disorder recovery. Although disorder reduced the superconducting critical temperature Tc, the concomitant electron scattering increased the…
The phase behavior of a single type of colloid C suspended in near-critical solvents is known to be very rich. Motivated in part by recent experiments we consider a mixture of two colloidal types C1 and C2 in a binary solvent close to its…
The superconducting properties of copper-sheathed MgB2 wires fabricated by conventional powder-in-tube techniques and the in-situ reaction procedure are analysed. The influence of the processing conditions and initial (1+x)Mg + 2B (x = 0,…
We prepared MgB$_{2-x}$Be$_{x}$ ($x=0$, 0.2, 0.3, 0.4, and 0.6) samples where B is substituted with Be. MgB$_{2}$ structure is maintained up to $x=0.6$. In-plane and inter-plane lattice constants were found to decrease and increase,…