Related papers: Synthesis of Mg(B$_{1-x}$C$_x$)$_2$ Powders

We synthesized polycrystalline MgB2 from a stoichiometric mixture of Mg and the 11 B isotope under different conditions. All the samples showed bulk superconductivity with Tc = 38~39 K. The samples containing the least amount of unreacted…

We succeeded in the fabrication of high-Jc MgB2/Fe wires applying the internal Mg diffusion (IMD) process with pure Mg core and SiC addition. A pure Mg rod with 2 mm diameter was placed at the center of a Fe tube, and the space between Mg…

Using Korringa-Kohn-Rostoker coherent-potential approximation in the atomic-sphere approximation (KKR-ASA CPA) method for taking into account the effects of disorder, Gaspari-Gyorffy formalism for calculating the electron-phonon coupling…

The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be…

Superconducting at 40 K MgB2 -samples were obtained by direct reaction from elements in molybdenum crucibles under argon pressure. Pressure allows to provide annealing at temperature up to 1400oC, that resulting in rise of Tc and…

A new route to the sintering of MgB2 has been identified, based on a reactive infiltration of liquid Mg on a powdered B preform. The technique allows to obtain large bulk manufacts in an inexpensive way, without the need of high pressure…

Magnesium diboride (MgB2) powder was mechanically alloyed by high energy ball milling with C to a composition of Mg(B0.95C0.05)2 and then sintered at 1000 C in a hot isostatic press. Milling times varied from 1 minute to 3000 minutes. Full…

Growth of carbon substituted magnesium diboride Mg(B1-xCx)2 single crystals with 0<x<0.15 is reported and the structural, transport, and magnetization data are presented. The superconducting transition temperature decreases monotonically…

Bulk MgB2 samples were prepared under different synthesis conditions and analyzed by scanning and transmission electron microscopy. The critical current densities were determined from the magnetization versus magnetic field curves of bulk…

The simultaneous addition of various Carbon based additives (in the present case B4C + SiC) to Mg and B powders has been introduced as a new concept in view of enhancing the superconducting parameters Bc2, Birr and Jc values of in situ…

The influence of the oxygen segregation into Mg-B-O inclusions (which are oxygen enriched as compared to the matrix material) and the formation of boron enriched phases (with near MgB12 composition) in MgB2 structure on pinning in magnesium…

We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…

Highly dense nanocrystalline MgB_2 bulk superconductors with distinctly improved pinning were prepared by mechanical alloying of Mg and B powders and hot compaction at ambient temperatures. The nanocrystalline samples reveal high critical…

Powdered and sintered MgB2 samples have been characterized through magnetic measurements performed from T = 5 K up to few degrees above the transition temperature of about 39 K. We found that the sintered samples behave as well-connected…

Bulk MgB2 - based materials with the following critical current densities (jc) in 1 T field: 570 kA/cm^2 at 10 K, 350 kA/cm^2 at 20 K and 40 kA/cm^2 at 30 K and in 10 T field: 650 A/cm^2 at 10 K have been high-pressure (HP) synthesized from…

An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter…

Bulk superconducting samples of MgB2 were prepared by solid state reaction of stoichiometric quantities of Mg turnings and B in a sealed Ta cylinder at 890 C for 2 hours. The as-synthesized MgB2 samples had a Tc of 39 K, as defined as the…

Superconducting Ag or Cu sheathed MgB2 wires have been fabricated by conventional powder-in-tube techniques. The in-situ reaction of Mg and B powders with atomic proportions of 1:2 and 1.33:2 inside Ag or Cu tubes at low temperatures have…

Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…

High-pressure (HP) synthesis and sintering are promising methods for manufacturing of the bulk MgB2 superconductive material. The available high-pressure apparatuses with 100 cm3 working volume can allow us to use the bulk MgB2 for…