Related papers: Enhanced flux pinning in neutron irradiated MgB2
In this letter we present the effect of neutron irradiation up to fluences of 3.9 1019 n/cm2 on the superconducting properties of MgB2. In order to obtain a disorder structure homogeneously distributed, the experiment was carried out on…
m-H loops for virgin and neutron irradiated bulk and powder samples of MgB_{2} were measured in the temperature range 5-30 K in magnetic field B<= 1 T. The irradiation at thermal neutron fluences 9*10^{13} and 4.5*10^{14} cm^{-2} caused…
We studied the influence of the disorder introduced in polycrystalline MgB2 samples by neutron irradiation. To circumvent self shielding effects due to the strong interaction between thermal neutrons and 10B we employed isotopically…
We report non-Cu critical current densities of 4.09 * 10^9 A/m^2 at 12 T and 2.27 * 10^9 A/m^2 at 15 T obtained from transport measurements on a Ti-alloyed RRP Nb3Sn wire after irradiation to a fast neutron fluence of 8.9 * 10^21 m^-2.…
We report the influence of crystalline defects introduced by 6 MeV $^{16}$O$^{3+}$ irradiation on the critical current densities J$_c$ and flux creep rates in 1.3 $\mu$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductor produced by…
Superconducting MgB2 strands with nanometer-scale SiC additions have been investigated systematically using transport and magnetic measurements. A comparative study of MgB2 strands with different nano-SiC addition levels has shown…
Polycrystalline MgB2 samples with 10 wt % silicon powder addition were prepared by an in-situ reaction process. Two different Si powders, one with coarse (44 mm) and the other with nano-size (<100 nm) particles were used for making samples.…
Strong pinning depends on the pinning force strength and number density of effective defects. Using hydrostatic pressure method, we demonstrate that hydrostatic pressure up to 1.2 GPa can significantly enhance flux pinning or Jc by a factor…
Doping of MgB2 by nano-SiC and its potential for improvement of flux pinning was studied for MgB2-x(SiC)x/2 with x = 0, 0.2 and 0.3 and a 10wt% nano-SiC doped MgB2 samples. Co-substitution of B by Si and C counterbalanced the effects of…
The effects of neutron irradiation on normal state and superconducting properties of epitaxial magnesium diboride thin films are studied up to fluences of 1020 cm-2. All the properties of the films change systematically upon irradiation.…
We report the synthesis and characterization of graphite (C) doped MgB2-xCx (x = 0.0, 0.1, 0.2 and 0.3) samples. The crystal structure and microstructural characterization have been investigated by x-ray diffractometer and transmission…
The upper critical field and flux pinning in MgB2 single crystals were investigated. The implications of these properties for technical applications are discussed and compared with transport properties of polycrystalline bulk samples and…
We present an extensive irradiation study involving five state-of-the-art Nb3Sn wires which were subjected to sequential neutron irradiation up to a fast neutron fluence of 1.6 * 10^22 m^-2 (E > 0.1 MeV). The volume pinning force of short…
SmFeAsO$_{1-x}$F$_x$ was irradiated in a fission reactor to a fast (E > 0.1 MeV) neutron fluence of 4x10^${21}$ m$^{-2}$. The introduced defects increase the normal state resistivity due to a reduction in the mean free path of the charge…
Critical current density is the key parameter for the practical application of superconductivity. In this study, 3 MeV proton irradiation experiments were conducted on HgBa$_2$Ca$_2$Cu$_3$O$_8$$_+$$_\delta$ single crystals to introduce…
We report on transport and magnetization measurements of the critical current density Jc in ErNi2B2C single crystals that show strongly enhanced vortex pinning at the Neel temperature TN and low applied fields. The height of the observed Jc…
A series of polycrystalline SmFeAs1-xOx bulks was prepared to systematically investigate the influence of sample density on flux pinning properties. Different sample densities were achieved by controlling the pelletizing pressure. The…
The effect of doping MgB2 with carbon nanotubes on transition temperature, lattice parameters, critical current density and flux pinning was studied for MgB2-xCx with x = 0, 0.05, 0.1, 0.2 and 0.3. The carbon substitution for B was found to…
Using the transport and magnetization measurements the influence of neutron irradiation at a fluence of 5x10$^{17}$ n cm$^{-2}$ on (B0.65C0.35)Ba1.4Sr0.6Ca2Cu3Oz has been investigated. The neutron irradiation was found to decrease critical…
The enhancement of the critical current density (Jc(H)) of carbon and nano-SiC doped MgB2 is presented and compared. The upper critical field (Hc2) being determined from resistivity under magnetic field experiments is though improved for…