Fatigue failure of crystalline materials is a difficult problem in science and engineering, and recent results have shown that fatigue crack growth can occur in intermittent jumps which have fat-tailed distributions. As fatigue crack…
A theoretical study based on dimensional analysis and fractal geometry of crack profiles is proposed to establish the relation between their fractal dimension D (1<D<2) and the parameters defining the fatigue crack propagation rate. The…
Fatigue fracture is one of the main causes of failure in structures. However, the simulation of fatigue crack growth is computationally demanding due to the large number of load cycles involved. Metals in the low cycle fatigue range often…
The growth of cracks combines materials science, fracture mechanics, and statistical physics. The importance of fluctuations in the crack velocity is fundamental since it signals that the crack overcomes local barriers such as tough spots…
We investigate the influence of microstructural traps in hydrogen-assisted fatigue crack growth. To this end, a new formulation combining multi-trap stress-assisted diffusion, mechanism-based strain gradient plasticity and a hydrogen- and…
Predicting potential risks associated with the fatigue of key structural components is crucial in engineering design. However, fatigue often involves entangled complexities of material microstructures and service conditions, making…
Cast and HIP'ed \textgamma-TiAl 4522XD is being developed for use in jet engine low pressure turbine blades, where temperature variations occur through the flight cycle. The effects of temperature variations on fatigue cracking were…
Recently acoustic signature of dislocation avalanches in HCP materials was found to be long tailed in size and energy, suggesting critical dynamics. Even more recently, the intermittent plastic response was found to be generic for micro-…
Fracture in aluminum alloys with precipitates involves at least two mechanisms, namely, ductile fracture of the aluminum-rich matrix and brittle fracture of the precipitates. In this work, a coupled crystal plasticity-phase field model for…
Fatigue crack growth is decisive for the design of thin-walled structures such as fuselage shells of air planes. The cold rolling process, used to produce the aluminium sheets this structure is made of, leads to anisotropic mechanical…
Fatigue behaviors of metal components by laser fusion suffer from scattering due to random geometrical defects (e.g., porosity, lack of fusion). Monitoring fatigue crack initiation and growth is critical, especially for laser-fused…
The extreme miniaturization in modern technology calls for deeper insights into the non-conventional, fluctuation dominated mechanics of materials at micro- to nano-scales. Both experiments and simulations show that sub-micron…
The paper at hand presents an in-depth investigation into the fatigue behavior of the high-strength aluminum alloy EN AW-7020 T6 using both experimental and numerical approaches. Two types of specimens are investigated: a dog-bone specimen…
A microstructure-based model that accounts for the effect of grain size has been developed to study the effect of grain size on the fatigue life of Inconel 718 alloys. The fatigue behavior of two alloys with different grain size was…
The properties of slow crack growth in brittle materials are analyzed both theoretically and experimentally. We propose a model based on a thermally activated rupture process. Considering a 2D spring network submitted to an external load…
Fatigue crack growth is usually a three-dimensional problem, but it is often simplified to two dimensions to reduce complexity. However, this study investigates the relationships between microscopic effects such as crack kinking, shear…
The increasing use of polymer composites in industry asks for the creation of better, faster and cost-effective methods to detect the damage state of such materials. This work presents the investigation of the phase decay , $\Delta{\Phi}$,…
Fatigue fracture in ductile materials, e. g. metals, is caused by cyclic plasticity. Especially regarding the high numbers of load cycles, plastic material models resolving the full loading path are computationally very demanding. Herein, a…
A novel variational framework to model the fatigue behavior of brittle materials based on a phase-field approach to fracture is presented. The standard regularized free energy functional is modified introducing a fatigue degradation…
Despite advances in manufacturing making metal functionally graded materials (FGMs) more common, numerical methods for predicting fracture in ductile functionally graded materials remain limited. In this work we study the crack propagation…