Related papers: Multifilamentary, in-situ Route, Cu-stabilized MgB…
Cu-stabilized 18-filament MgB2 tapes with NbZr buffer have been fabricated by using powder-in-tube technique. The phase composition and microstructure were examined by X-ray diffraction and optical microscopy. Transport critical current…
The critical current densities of MgB2 monofilamentary strands with and without SiC additions were measured at 4.2 K. Additionally, magnetic Jc at B = 1 T was measured from 4.2 K to 40 K. Various heat treatment times and temperatures were…
MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density…
Multifilamentary MgB2/Fe wires and tapes with high transport critical current densities have been fabricated using a straightforward powder-in-tube (PIT) process. After annealing, we measured transport jc values up to 1.1 * 105 A/cm2 at 4.2…
Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires…
An advanced internal Mg infiltration method (AIMI) in this paper has been shown to be effective in producing superconducting wires containing dense MgB2 layers with high critical current densities. In this study, the in-field critical…
Mono- and multifilamentary MgB2/Fe tapes and wires with high transport critical current densities have been prepared using the powder-in-tube (PIT) process. The fabrication details are described. The effect of powder grain sizes and…
The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…
A racetrack coil using MgB2/Cu strand has been fabricated and tested for transport current density at 4.2 K in self field. The monofilamentary strand was 1.0 mm OD and insulated with S-glass braid. Eighty turns of strand (42 m) were wound…
Critical current density was measured at 4.2 K for MgB2 strands with and without SiC additions. In some cases measurements were performed on longer (1 m) samples wound on barrels, and these were compared to magnetic measurements. Most…
Three solenoids have been wound and with MgB2 strand and tested for transport properties. One of the coils was wound with Cu-sheathed monofilamentary strand and the other two with a seven filament strand with Nb-reaction barriers, Cu…
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient…
The MgB2 coated superconducting tapes have been fabricated on textured Cu (0 0 1) and polycrystalline Hastelloy tapes using coated conductor technique, which has been developed for the second generation high temperature superconducting…
The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the…
MgB2 wires and tapes suffer from a limitation of the transport current densities, especially at low field, due to an unsufficient thermal stabilization caused by hot spots from a non-homogeneous microstructure, the presence of secondary…
We report on the preparation of dense monofilamentary MgB2/Ni and MgB2/Fe tapes with high critical current densities. In annealed MgB2/Ni tapes, we obtained transport critical current densities as high as 2.3*105 A/cm2 at 4.2 K and 1.5 T,…
We report the successful fabrication of single-filament composite MgB2/SUS ribbons, as an ultra-robust conductor type, employing the powder-in-tube (PIT) process, by swaging and cold rolling only. The remarkable transport critical current…
Transport and thermodynamic properties of a sintered pellet of the newly discovered $MgB_2$ superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition…