Related papers: Thick MgB2 film with (101) oriented micro-crystals
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
Upper critical fields of several magnesium diboride thin films were measured up to 28 T at the Grenoble High Magnetic Field Laboratory (GHMFL) in Grenoble and up to 60 T at the Laboratoire National des Champs Magnetiques Pulses (LNCMP) in…
1.8 micrometer-thick magnesium hydride films were synthesized in a single-step process by reactive plasma-assisted sputtering. The MgH2 thin films, which were deposited on two types of flexible surfaces (namely graphite and polyimide foils)…
A large anisotropy in the upper critical field (H$_{C2}$) is observed for MgB$_{2}$ films grown in situ by a pulsed laser deposition process involving growth and annealing of Mg and B multilayers. Measurements of resistivity as a function…
The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron…
A complexing molecule electrodeposition technique has been developed for the deposition of low cost, lightweight MgB2 films, for the first time. Different deposition parameters such as bath composition, deposition potential, current…
Superconducting thin films of magnesium diboride (MgB$_2$) were prepared on MgO (001) substrate by a molecular beam epitaxy (MBE) method with the co-evaporation conditions of low deposition rate in ultra-high vacuum. The structural and…
We review the thin film growth, chemistry, and physical properties of Group 4-6 transition-metal diboride (TMB2) thin films with AlB2-type crystal structure (Strukturbericht designation C32). Industrial applications are growing rapidly as…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
A new method for preparation of single crystals of the superconducting intermetallic MgB2 compound from a Mg-Cu-B melt flux is presented. The high vapour pressure of Mg at elevated temperature is a serious challenge of the preparation…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
We develop the multi-band BCS model of superconductivity in the ultrathin films using the orthogonal tight-binding approximation for constructing the electron wavefunctions. This allows for relatively simple determination of the band…
We present experimental results of the upper critical fields $H_{\rm c2}$ of various MgB$_2$ thin films prepared by the molecular beam epitaxy, multiple-targets sputtering, and co-evaporation deposition apparatus. Experimental data of the…
Ruthenium dioxide (RuO$_2$) thin films were synthesized by Chemical Solution Deposition (CSD) on silicon substrates using only water and acetic acid as solvents. The microstructure, phase-purity, electrical and optical properties as well as…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
We report on the preparation and the physical properties of superconducting (TaNb)_1-x(ZrHfTi)_x high-entropy alloy films. The films were prepared by means of magnetron sputtering at room temperature, with x ranging from 0 to 1 with an…
We report on the transport, magnetization, and scanning tunneling spectroscopy measurements on c-axis oriented thin films of MgB2 irradiated with high energy heavy ions of uranium and gold. We find a slight shift in the irreversibility and…
As-grown superconducting MgB_2 thin films have been grown on SrTiO_3(001), MgO(001), and Al_2O_3(0001) substrates by a molecular beam epitaxy (MBE) method with novel co-evaporation conditions of low deposition rate in ultra-high vacuum. The…