The effective adhesive properties of heterogeneous thin films are characterized through a combined experimental and theoretical investigation. By bridging scales, we show how variations of elastic or adhesive properties at the microscale…
Peeling is one of the most common detachment mechanisms adopted in industrial applications. However, although several experimental investigations have proven the possible occurrence of relative sliding at the interface close to the peeling…
The functionality of adhesives relies on their response under the application of a load. Yet, it has remained a challenge to quantitatively relate the macroscopic dynamics of peeling to the dissipative processes inside the adhesive layer.…
We formulate a theoretical model of the shear failure of a thin film tethered to a rigid substrate. The interface between film and substrate is modeled as a cohesive layer with randomly fluctuating shear strength/fracture energy. We…
Thin elastic sheets and membranes are known to wrinkle when they are stretched -- the associated physics is highly non-linear. The mechanics of thin films that exhibit unusual behavior upon stretching, when they possess auxetic structure,…
A hydrostatically stressed soft elastic film circumvents the imposed constraint by undergoing a morphological instability, the wavelength of which is dictated by the minimization of the surface and the elastic strain energies of the film.…
Adhesive peeling of a thin elastic film from a substrate is a classic problem in mechanics. However, many of the investigations on this topic to date have focused on peeling from substrates with flat surfaces. In this paper, we study the…
We study the indentation of a thin elastic film floating at the surface of a liquid. We focus on the onset of radial wrinkles at a threshold indentation depth and the evolution of the wrinkle pattern as indentation progresses far beyond…
A confined incompressible elastic film does not deform uniformly when subjected to adhesive interfacial stresses but with undulations which have a characteristic wavelength scaling linearly with the thickness of the film. In the classical…
We study the peeling process of a thin viscoelastic tape from a rigid substrate. Two different boundary conditions are considered at the interface between the tape and the substrate: stuck adhesion, and relative sliding in the presence of…
Propagation of a viscous fluid beneath an elastic sheet is controlled by local dynamics at the peeling front, in close analogy with the capillary-driven spreading of drops over a precursor film. Here we identify propagation laws for a…
We report a novel mode of oscillatory crack propagation when a cutting tip is driven through a thin brittle polymer film. The phenomenon is so robust that it can easily be reproduced at hand (using CD packaging material for example).…
Blisters, delaminated regions that form in multilayered structures under compressive stresses, are observed across a wide range of length scales, from two-dimensional materials to protective coatings and laminated composites. Far from being…
Cohesive granular materials, like wet sand, retain their shape before yielding under stress. This solid-like behavior is associated with elasticity. As the loading increases, the material typically flows. However, cohesive materials can…
Using a high-speed camera, we follow the propagation of the detachment front during the peeling of an adhesive tape from a flat surface. In a given range of peeling velocity, this front displays a multiscale unstable dynamics, entangling…
Crumpling of a thin film leads to a unique stiff yet lightweight structure. The stiffness has been attributed to a complex interplay between four basic elements - smooth bends, sharp folds, localized points (developable cones), and…
Thin layers of elastomers bonded to two rigid plates demonstrate unusual failure response. Historically, it has been believed that strongly-bonded layers fail by two distinct mechanisms: (i) internal/external penny-shaped crack nucleation…
When a flexible plate is peeled off a thin and soft elastic film bonded to a rigid support, uniformly spaced fingering patterns develop along their line of contact. While, the wavelength of these patterns depends only on the thickness of…
We study the interaction between two cracks propagating quasistatically during the tearing of a thin brittle sheet. We show that the cracks attract each other following a path described by a power law resulting from the competition between…
We study the nucleation and development of crack patterns in thin composite fibers under tension in this work. A fiber comprises an elastic core and an outer layer of a weaker brittle material. In recent tensile experiments on such…