Related papers: Stress-Dependent Magnetoimpedance in Co-Based Amor…
The effect of tensile stress on magnetoimpedance (MI) in CoMnSiB amorphous wires at microwave frequencies (0.5-3 GHz) is investigated both experimentally and theoretically. In the presence of the dc bias magnetic field of the order of the…
We demonstrate composite media with ferromagnetic wires that exhibit a frequency region at the microwave regime with scattering spectra strongly dependent on an external magnetic field or stress. These tunable composite materials have…
Systematic measurements of stress-impedance (SI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The…
New types of tunable composite materials are considered, the effective microwave permittivity of which may depend on an external dc magnetic field or tensile stress. The composites consist of short pieces of conductive ferromagnetic…
Systematic measurements of stress impedance (SI) and magneto-impedance (MI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at…
High frequency [1-500 MHz] measurements of the magnetoimpedance (MI) of glass-coated Co$_{69.4}$Fe$_{3.7}$B$_{15.9}$Si$_{11}$ microwires are carried out with various metal-to-wire diameter ratios. A twin-peak, anhysteretic behaviour is…
This paper concerns the theoretical and experimental investigation of the magneto-impedance (MI) effect in amorphous wires in terms of the surface impedance tensor. Physical concepts of MI and problems of significant practical importance…
The effective permittivity of composites containing ferromagnetic microwires has been analysed within a one-particle approximation, by considering a wire piece as an independent scatterer and solving the scattering problem with the…
A model describing the influence of torsion stress on the giant magnetoimpedance in amorphous wires with negative magnetostriction is proposed. The wire impedance is found by means of the solution of Maxwell equations together with the…
High frequency [1-500 MHz] measurements of the Magneto-Impedance (MI) of glass-covered Co$_{69.4}$Fe$_{3.7}$B$_{15.9}$Si$_{11}$ microwires are carried out with various metal-to-wire diameter ratios. A twin-peak, anhysteretic behaviour is…
The resistive and reactive components of magneto-impedance (MI) for Finemet/Copper/Finemet sandwiched structures based on stress-annealed nanocrystalline Fe75Si15B6Cu1Nb3 ribbons as functions of different fields (longitudinal and…
A combination of micro-Raman spectroscopy and micro-XPS (X-ray photo-electron spectroscopy) mapping on statically deflected p-type silicon cantilevers is used to study the mechanical stress dependence of the Fermi level pinning at an…
The optimization of high frequency giant magnetoimpedance (GMI) effect and its magnetic field sensitivity in melt-extracted Co69.25Fe4.25Si13B12.5Nb1 amorphous microwires, through a multi-step Joule annealing (MSA) technique, was…
A study of magnetic hysteresis and Giant magnetoimpedance (GMI) in amorphous glass covered Co-Si-B and Co-Mn-Si-B wires is presented. The wires, about 10 microns in diameter, were obtained by glass-coated melt spinning technique. Samples…
Magnetoimpedance, MI, change due to surface modification of the sensitive element caused by biofluids was studied with the aim of creating a robust sensor capable of separating the chemical surface modification from the sensing process. A…
In this research project we propose a new composite medium, which can visualise the mechanical stress at any stage: before and after damage. The main feature of the proposed stress-tuneable composite is its permittivity (dielectric…
Recent measurements of the magnetoimpedance (at a fixed frequency of 1 MHz) of cobalt-rich wires subjected to torsion stress show an asymmetry as a function of torsion angle stemming from residual anisotropies induced during wire…
Magneto-impedance (MI) of soft ferromagnetic materials is a sensitive function of the amplitude and frequency of exciting a.c magnetic field. MI (Z) of amorphous ferromagnetic ribbon of nominal composition Fe73.5Nb3 Cu1 Si13.5 B9 is…
An influence of a time dependent external tensile stress on the remagnetization process of a bistable wire is investigated experimentally and numerically. The dependence of the magnetization on the frequency of the tensile stress is…
The magneto-impedance (MI) of glass-coated Fe-Ni-Cu microwires was investigated for longitudinal radio-frequency (RF) currents up to a frequency of 200 MHz using an RF lock-in amplifier method. The MI, defined as DZ/Z =…