Related papers: Study of the SmBaCuO solid solutions decomposition…
Thermochemical characteristics of Nd1+xBa2-xCu3Oy solid solutions were studied by solution calorimetry. Dependences of formation enthalpies from Nd content were constructed. It was established that decomposition of solid solution on the…
A series of polycrystalline SmO1-xFxFeAs bulks (x=0.15, 0.2, 0.3 and 0.4) were prepared by the conventional solid state reaction. Resistivity, susceptibility, magnetic hysteresis, critical current density and microstructure of these samples…
Bulk superconductor samples of YBa2Cu3-xCoxO7-{\delta} with x = 0, 0.01, 0.03, 0.05 are synthesized by solid-state reaction route. Both x-ray diffraction and electron microscopy have been employed to study the phase identification,…
Samples of YBa2-xSrxCu3O7-d (x = 0.0, 0.50, 1.0) series were synthesized by solid-state reaction and first annealed in flowing O2 gas. All samples crystallized in orthorhombic structure, where orthorhombic distortion was found to decrease…
Solid solutions of Sr1-xLaxPbO3 (x = 0, 0.05, 0.10, 0.15 and 0.20) were synthesized with the help of high pressure. Temperature (T) dependences of the resistivity r and differential thermoelectric power S were measured. All samples…
The dependence of the critical current density Jc on hydrostatic pressure to 0.6 GPa is determined for a single 25-degree [001]-tilt grain boundary in a bicrystalline ring of nearly optimally doped melt-textured YBa2Cu3Ox. Jc is found to…
A scan of the superconductor -- nonsuperconductor transformation in single crystals YBa_2Cu_3O_{6+x} (x about 0.37) was done in two alternative ways, namely, by applying the magnetic field and by reducing the hole concentration through the…
Single crystals of Na$_{0.5}$CoO$_2$ were obtained through a flux method followed by de-intercalation of sodium. The Na$_{0.5}$CoO$_2$ samples were found to be vulnerable to water in the air and a hydration process in which H$_2$O molecules…
In type-II superconductors, in the regime of very high applied current density, an abrupt transition is experimentally observed from the mixed state to a highly dissipative regime, probably the normal state. This provokes a high voltage…
We present high-resolution capacitance dilatometry studies from 5 - 500 K of untwinned YBa2Cu3Ox (Y123) single crystals for x ~ 6.95 and x = 7.0. Large contributions to the thermal expansivities due to O-ordering are found for x ~ 6.95,…
An increasing current through a superconductor can result in a discontinuous increase in the differential resistance at the critical current. This critical current is typically associated either with breaking of Cooper-pairs (de-pairing) or…
Using the Green's function of the 3D heat equation, we develop an analytical account of the thermal behaviour of superconducting films subjected to electrical currents larger than their critical current in the absence of an applied magnetic…
A safe, simple and easily scaleable one-step sintering method is proposed to fabricate newly discovered superconductors of SmO1-xFxFeAs. Superconducting transition with the onset temperature of 54.6 K and high critical fields Hc2(0) >=200 T…
The linear compressibilities and the thermal expansion of an untwinned, nearly optimal doped YBa2Cu3O6.94 single crystal were measured along the three crystallographic axes with a high-resolution dilatometer mounted in a high-pressure cell.…
The specific heat of Nd(Y)Ba2Cu3Ox single crystals without substitution of Nd for Ba has been measured for various oxygen contents. In comparison with YBa2Cu3Ox, the maximum attainable transition temperature of the crystals is about 4 K…
Ag-sheathed SmFeAsO0.7F0.3 (Sm-1111) superconducting wires were prepared by a one-step solid state reaction at temperatures as low as 850~900C, instead of commonly used temperatures of 1150~1250C. The X-ray diffraction pattern of the…
The temperature dependence of the anisotropy of the superconducting state parameters, {\gamma}, was studied by torque magnetometry for the high temperature superconductor SmBa2Cu3Ox in magnetic fields of up to 9 T. The measurements were…
Samples of Y0.4Pr0.6Ba2-xSrxCu3O7 have been synthesized by a solid- state reaction route. The samples with x = 0.60 crystallize in an orthorhombic structure (with orthorhombic distortion decreasing with increasing x), while the samples with…
Detailed measurements of the critical current density jc of YBa2Cu3O7 films grown by pulsed laser deposition reveal the increase of jc as function of the filmthickness. Both this thickness dependence and the field dependence of the critical…
A rapid decrease in the critical current density (Jc) of YBa2Cu3O7-x (YBCO) films with increasing film thickness has been observed for multiple YBCO growth processes. While such behavior is predicted from 2D collective pinning models under…