Related papers: Study on the formation of MgB2 phase
We report the preparation of Mg$_{1-x}$B$_{2}$ (0$\le$x$\le$0.5) compounds with the nominal compositions. Single phase MgB$_{2}$ was obtained for x=0 sample. For 0$<$x$\le$0.5, MgB$_{4}$ coexists with "MgB$_{2}$" and the amount of MgB$_{4}$…
We report on the phase formation and the superconducting properties in the NbS$_2$ system. Specifically, we have performed a series of standardized solid-state syntheses in this system, which allow us to establish a comprehensive synthesis…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot…
We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of…
Measurements of temperature-dependent resistance and magnetization under hydrostatic pressures up to 2.13 GPa are reported for single-crystalline, superconducting BaBi$_3$. A temperature - pressure phase diagram is determined and the…
We studied the influence of sample preparation and defects in the superconducting properties samples using atomic ratios of Mg:B=1:1 and Mg:B=1:2. Samples were characterized by SEM, and XRD, and the magnetization properties were examined in…
Following long-standing predictions associated with hydrogen, high-temperature superconductivity has recently been observed in several hydride-based materials. Nevertheless, these high-$T_c$ phases only exist at extremely high pressures,…
MAB phases (MABs) are atomically-thin laminates of ceramic/metallic-like layers, having made a breakthrough in the development of 2D materials. Though theoretically offering a vast chemical and phase space, relatively few MABs have yet been…
Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin…
The influence of the nature of the boron precursor on the superconducting properties of polycrystalline MgB2 was studied. Critical current densities for the MgB2 made from high purity amorphous boron are at least a factor of three higher…
We studied the effect of disorder on the superconducting properties of polycrystalline MgB_2 by specific-heat measurements. In the pristine state, these measurements give a bulk confirmation of the presence of two superconducting gaps with…
We have performed a comparative study of two thin films of magnesium diboride (MgB2) grown by different techniques. The critical current density at different temperatures and magnetic fields was evaluated from magnetisation curves, the…
We present data on temperature-dependent anisotropy of the upper critical field of MgB$_2$ obtained from the analysis of measurements on high purity, low resistivity polycrystals. The anisotropy decreases in a monotonic fashion with…
In the search for MgB2-like phonon-mediated superconductors we have carried out a systematic density functional theory study of the Ca-B system, isoelectronic to Mg-B, at ambient and gigapascal pressures. A remarkable variety of candidate…
MgB2 superconducting wires with critical temperature Tc approaching 40 K were used for preparation of MgB2/Ag and MgB2/In junctions. The differential conductance vs. voltage characteristics of N-S junctions exhibit clear contribution of…
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…
Growth parameters play a significant role in the crystal quality and physical properties of layered materials. Here we present a case study on a van der Waals magnetic NbFeTe2 material. Two different types of polymorphic NbFeTe2 phases,…
We report on the synthesis and on basic superconducting properties of a completely new Mo_2Re_3B ternary boride. The crystal structure of the Mo_2Re_3B compound is characterised by Pmmm space group and the cell parameters: a=11.626 A,…
This work examines the oxygenation process of polycrystalline powder of YBa$_2$Cu$_3$O$_{6+\delta}$ superconductor material through constant temperature thermogravimetric analysis. Starting from completely deoxygenated samples ($\delta$ =…