Related papers: Dependence of Maximum Trappable Field on Supercond…
A trapped field of over 1 T at 5 K and 0.5 T at 20 K has been measured between a stack of magnetized cylinders of bulk polycrystalline Ba0.6K0.4Fe2As2 superconductors 10 mm in diameter and 18 mm in combined thickness. The trapped field…
High temperature superconducting (HTS) tape can be cut and stacked to generate large magnetic fields at cryogenic temperatures after inducing persistent currents in the superconducting layers. A field of 17.7 T was trapped between two…
The ability of stacks of superconducting tapes to trap large magnetic fields makes them ideal candidates for creating powerful permanent magnets of compact size and mass. Experimentally, several techniques are used to trap the maximum…
Trapped fields of over 20 T are, in principle, achievable in bulk, single-grain high temperature cuprate superconductors. The principle barriers to realizing such performance are, firstly, the large tensile stresses that develop during the…
The distribution of the current density and the profile of the trapped magnetic field of a superconducting disk magnetized by uniform field are calculated from first principles. The effect of the superconducting parameters is taken into…
We fabricated a compact (13$\times$12$\times$12.5 mm${^3}$) trapped-field magnet by stacking 200 pieces of EuBa${_2}$Cu${_3}$O${_7}$ coated conductors with BaHfO${_3}$ nanorods as artificial pinning centers. It was magnetized by…
Improved trapped fields are reported for bulk melt-textured YBa2Cu3O7-x (YBCO) material in the temperature range between 20 K and 50 K. Trapped fields up to 12.2 T were obtained at 22 K on the surface of single YBCO disks (with Ag and Zn…
A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a…
The ability of large grain, REBa$_{2}$Cu$_{3}$O$_{7-\delta}$ [(RE)BCO; RE = rare earth] bulk superconductors to trap magnetic field is determined by their critical current. With high trapped fields, however, bulk samples are subject to a…
The distributions of the magnetic field and temperature in a superconducting-disk magnetized by pulse field, and the levitation force between this disk and a permanent magnet are calculated from first principles. The calculation is based…
Superconducting bulk (RE)Ba$_2$Cu$_3$O$_{7-x}$ materials (RE-rare earth elements) have been successfully used to generate magnetic flux densities in excess of 17 T. This work investigates an alternative approach by trapping flux in stacks…
We have developed disk-shaped MgB2 bulk superconducting magnets (20, 30 mm in diameter, 10 mm in thickness) using the in-situ process from Mg and B powders and evaluated the temperature dependence of trapped magnetic field. A pair of two…
Porous silicon, obtained by electrochemical etching, has been used as a substrate for the growth of nanoperforated Nb thin films. The films, deposited by UHV magnetron sputtering on the porous Si substrates, inherited their structure made…
Recent discoveries of superconductivity in hydrogen-rich compounds stabilized by high pressures have shown that a critical temperature of superconductivity Tc can reach near room temperature values. The current studies focus on the search…
The temperature and field dependences of the trapped magnetic fields and of the frozen magnetoresistance of (Pb)Bi-Sr-Ca-Cu-O ceramics and Bi-based magnetron films are investigated. It is found that in the resistive transition region of…
Strontium intercalation between van der Waals bonded layers of topological insulator Bi2Se3 is found to induce superconductivity with a maximum Tc of 2.9 K. Transport measurement on single crystal of optimally doped sample Sr0.1Bi2Se3 shows…
Electrical magnetoresistance and tunnel diode oscillator measurements were performed under external magnetic fields up to 41 T applied along the crystallographic b-axis (hard axis) of UTe$_2$ as a function of temperature and applied…
High-temperature conventional superconductivity in hydrogen-rich materials under high pressure has been reportedly found in twelve different compounds in recent years. However, the experimental evidence on which these claims are based has…
It is shown that a multilayer comprised of alternating thin superconducting and insulating layers on a thick substrate can fully screen the applied magnetic field exceeding the superheating fields $H_s$ of both the superconducting layers…
The discovery of superconductivity in 3$d$-transition metal compounds with strong magnetism is interesting but rare. Especially for Mn-based compounds, there exist only very limited materials that show superconductivity. Here, we report the…