Far-infrared reflectivity studies on the polycrystalline intermetallic compound MgB_2 with a superconducting transition temperature T_c=39 K were performed at temperatures 20 K to 300 K. We observe a significant raise of the…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
Single crystals of MgB2 have been grown with a high-pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB9 ternary nitride. The crystals are of a size up to 2x1x0.1mm3 with a weight up to 230 micrograms.…
Single crystals of MgB2 have been grown at high pressure via the peritectic decomposition of MgNB9. The crystals are of a size up to 1.5x0.9x0.2 mm3 with a weight up to 0.23 mg, and typically have transition temperatures between 37 and 39…
An instrument has been constructed to measure a large range of magnetostriction and thermal expansion between room temperature and 4 K in a superconductive split-coil magnet, that allows investigation in magnetic fields up to 12 T. The very…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
A new method for preparation of single crystals of the superconducting intermetallic MgB2 compound from a Mg-Cu-B melt flux is presented. The high vapour pressure of Mg at elevated temperature is a serious challenge of the preparation…
An anisotropic lattice anomaly near the superconducting transition temperature, Tc, was observed in MgB2 by high-resolution neutron powder diffraction. The a-axis thermal expansion becomes negative near Tc, while the c-axis thermal…
We studied the effect of disorder on the superconducting properties of polycrystalline MgB_2 by specific-heat measurements. In the pristine state, these measurements give a bulk confirmation of the presence of two superconducting gaps with…
The linear compressibilities and the thermal expansion of an untwinned, nearly optimal doped YBa2Cu3O6.94 single crystal were measured along the three crystallographic axes with a high-resolution dilatometer mounted in a high-pressure cell.…
The thermal expansion of the wide band gap semiconductor MgSiN$_{2}$ has been determined using density functional calculations in combination with the quasi-harmonic approximation. We find that the thermal expansion is rather small in good…
Thermal expansion of {\alpha}-rhombohedral boron ({\alpha}-B12) and two isostructural boron-rich pnictides (B12P2 and B12As2) has been studied between 298 and 1280 K by high-temperature synchrotron X-ray diffraction. For all studied phases…
We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…
The specific heat of polycrystalline Mg$^{11}$B$_{2}$ has been measured with high resolution ac calorimetry from 5 to 45 K at constant magnetic fields. The excess specific heat above T$_{c}$ is discussed in terms of Gaussian fluctuations…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
We discuss the important aspects of synthesis and crystal growth of MgB2 under high pressure (P) and temperature (T) in Mg-B-N system, including the optimisation of P-T conditions for reproducible crystal growth, the role of liquid phases…
The p-V-T equation of state of magnesium metal has been measured up to 20 GPa and 1500 K using both multianvil and opposite anvil techniques combined with synchrotron X-ray diffraction. To fit the experimental data, the model of…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…