Related papers: Effect of two bands on critical fields in MgB2 thi…
In this paper, we analyze the upper critical field of four MgB2 thin films, with different resistivity (between 5 to 50 mWcm) and critical temperature (between 29.5 to 38.8 K), measured up to 28 Tesla. In the perpendicular direction the…
Critical fields of four MgB2 thin films with a normal state resistivity ranging from 5 to 50 mWcm and Tc from 29.5 to 38.8 K were measured up to 28 T. Hc2(T) curves present a linear behavior towards low temperatures. Very high critical…
We have performed a comparative study of two thin films of magnesium diboride (MgB2) grown by different techniques. The critical current density at different temperatures and magnetic fields was evaluated from magnetisation curves, the…
We develop the multi-band BCS model of superconductivity in the ultrathin films using the orthogonal tight-binding approximation for constructing the electron wavefunctions. This allows for relatively simple determination of the band…
Magnetotransport measurements are presented on polycrystalline MgB2 samples. The resistive upper critical magnetic field reveals a temperature dependence with a positive curvature from Tc = 39.3 K down to about 20 K, then changes to a…
Upper critical fields of several magnesium diboride thin films were measured up to 28 T at the Grenoble High Magnetic Field Laboratory (GHMFL) in Grenoble and up to 60 T at the Laboratoire National des Champs Magnetiques Pulses (LNCMP) in…
We present experimental results of the upper critical fields $H_{\rm c2}$ of various MgB$_2$ thin films prepared by the molecular beam epitaxy, multiple-targets sputtering, and co-evaporation deposition apparatus. Experimental data of the…
We report a significant enhancement of the upper critical field $H_{c2}$ of different $MgB_2$ samples alloyed with nonmagnetic impurities. By studying films and bulk polycrystals with different resistivities $\rho$, we show a clear trend of…
Magneto-resistivity of a c-axis oriented MgB$_{2}$ thin film was studied in perpendicular and parallel magnetic fields up to $\sim $23 T with temperatures down to 0.38 K. Resistive critical magnetic fields were determined. Large separations…
High-quality epitaxial MgB2 thin films prepared by pulsed laser deposition with Tc = 39 K offer the opportunity to study the anisotropy and robustness of the superconducting state in magnetic fields. We measure the in-plane electrical…
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated in magnetic fields up to 16 T. The upper critical field of the major fraction of the investigated sample was determined…
The angular dependence of the upper critical field Hc2 of MgB2 single crystals is studied at various temperatures by means of specific heat and transport measurements in magnetic fields up to 17 T. Clear deviations from Ginzburg-Landau…
The anisotropy of MgB2 is still under debate: its value, strongly dependent on the sample and on the measuring method, ranges between 1.2 and 13. In this work we present our results on a MgB2 c-oriented superconducting thin film. To…
According to the crystal structure of MgB$_{2}$ and band structure calculations quasi-two-dimensional (2D) boron planes are responsible for the superconductivity. We report on critical fields and resistance measurements of 30 nm thick…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated by transport, ac susceptibility and dc magnetization measurements in magnetic fields up to 16 T covering a temperature…
We have measured the normal state temperature dependence of the Hall effect and magnetoresistance in epitaxial MgB2 thin films with variable disorders characterized by the residual resistance ratio RRR ranging from 4.0 to 33.3. A strong…
We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…
We investigated the effect of alloying on the upper critical field $H_{c2}$ in 12 $MgB_2$ films, in which disorder was introduced by growth, carbon doping or He-ion irradiation, finding a significant $H_{c2}$ enhancement in C-alloyed films,…
A large anisotropy in the upper critical field (H$_{C2}$) is observed for MgB$_{2}$ films grown in situ by a pulsed laser deposition process involving growth and annealing of Mg and B multilayers. Measurements of resistivity as a function…