We report the preparation of Mg$_{1-x}$B$_{2}$ (0$\le$x$\le$0.5) compounds with the nominal compositions. Single phase MgB$_{2}$ was obtained for x=0 sample. For 0$<$x$\le$0.5, MgB$_{4}$ coexists with "MgB$_{2}$" and the amount of MgB$_{4}$…
The dependence of Tc on nearly hydrostatic pressure has been measured for an isotopically pure (11B) MgB2 sample in a helium-loaded diamond-anvil-cell to nearly 20 GPa. Tc decreases monotonically with pressure from 39.1 K at ambient…
The high field magnetization and magneto transport measurements are carried out to determine the critical superconducting parameters of MgB2-xCx system. The synthesized samples are pure phase and the lattice parameters evaluation is carried…
Magnetic ions (Mn) were substituted in MgB_2 single crystals resulting in a strong pair-breaking effect. The superconducting transition temperature, T_c, in Mg_{1-x}Mn_xB_2 has been found to be rapidly suppressed at an initial rate of 10…
We grew (Hg,Re)Ba$_2$Ca$_2$Cu$_3$O$_{8+\delta}$ ((Hg,Re)1223) single crystals with good reproducibility via the single-step flux method using monoxides as raw materials. A double-sealing method using a thick-walled quartz tube and a…
Single crystals of Ba(Fe_(1-x)Mn_x)_2As_2, 0<x<0.148, have been grown and characterized by structural, magnetic, electrical transport and thermopower measurements. Although growths of single crystals of Ba(Fe_(1-x)Mn_x)_2As_2 for the full…
The system MgxB2 has been investigated to investigate possible nonstoichiometry in MgB2. When synthesized at 850oC, MgB2 is a line compound with a possible Mg vacancy content of about 1%. Small changes in lattice constants as a function of…
We present the results of directional point-contact spectroscopy in state-of-the-art Mg_{1-x}Al_xB_2 and Mg(B_{1-y}C_{y})_2 single crystals produced at ETH, Zurich. Fitting the conductance curves of our point contacts, that always feature…
We prepared MgB$_{2-x}$Be$_{x}$ ($x=0$, 0.2, 0.3, 0.4, and 0.6) samples where B is substituted with Be. MgB$_{2}$ structure is maintained up to $x=0.6$. In-plane and inter-plane lattice constants were found to decrease and increase,…
F-substituted ROBiS2 (R = La, Ce, Nd) superconducting single crystals with different F concentration were grown successfully using CsCl/KCl flux. All the obtained single crystals had a plate-like shape with a well-developed ab-plane of 1-2…
Superconductivity is achieved in Nd1-xCexOBiS2 via electron doping using mixed-valence Ce ions. Single crystals with x = 0.2, 0.3, 0.4, and 0.5 are generated using a CsCl flux method. Plate-like single crystals with dimensions of 0.8 0.8…
A comprehensive study of the effects of carbohydrate doping on the superconductivity of MgB2 has been conducted. In accordance with the dual reaction model, more carbon substitution is achieved at lower sintering temperature. As the…
We discuss the irreversible magnetic properties of self-flux grown Ba(Fe1-xCox)2As2 single crystals for a wide range of concentrations covering the whole phase diagram from the underdoped to the overdoped regime, x=0.038, 0.047, 0.058,…
The effect of nano-C doping on the microstructure and superconducting properties of Fe-sheathed MgB2 tapes prepared through the in-situ powder-in-tube method was studied. Heat treatment was performed at a low temperature of 650C for 1 h.…
Despite the intense activity in the year since the discovery of superconductivity in MgB2, key parameters, in particular the upper and lower critical fields Hc2 and Hc1 and their anisotropies, are not well-established, largely because of…
Polarisation-resolved Raman scattering measurements were performed on MgB_2 single crystals to determine the magnitude, symmetry and temperature dependence of the superconducting gap. A single sharp peak due to Cooper pair breaking appears…
We studied the influence of sample preparation and defects in the superconducting properties samples using atomic ratios of Mg:B=1:1 and Mg:B=1:2. Samples were characterized by SEM, and XRD, and the magnetization properties were examined in…
The lattice parameters of MgB2 up to pressures of 8 GPa were determined using high-resolution x-ray powder diffraction in a diamond anvil cell. The bulk modulus, B0, was determined to be 151 +-5 GPa. Both experimental and first-principles…
We report the effect of adipic acid (C6H10O4) doping on lattice parameters, microstructure, critical temperature (Tc), current density (Jc), and irreversibility field (Hirr) for MgB2 superconductor. Actual carbon (C) substitution level for…
The temperature dependent resistivity of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (x = 0.23, 0.25, 0.28 and 0.4) single crystals and the angle dependent resistivity of superconducting Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystals were measured in…