By doping MgB_2 superconductor with SiC nano-particles, we have successfully introduced pinning sites directly into the crystal lattice of MgB_2 grains (intra-grain pinning). It became possible due to the combination of counter-balanced Si…
We discuss the important aspects of synthesis and crystal growth of MgB2 under high pressure (P) and temperature (T) in Mg-B-N system, including the optimisation of P-T conditions for reproducible crystal growth, the role of liquid phases…
We have performed a comparative study of two thin films of magnesium diboride (MgB2) grown by different techniques. The critical current density at different temperatures and magnetic fields was evaluated from magnetisation curves, the…
The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT…
MgB2/Fe tapes with 2.5-15 at.% ZrB2 additions were prepared through the in situ powder-in-tube method. Compared to the pure tape, a significant improvement in the in-field critical current density Jc was observed, most notably for 10 at.%…
We present the fabrication and test results of Hot-Isostatic-Pressed (HIPed) Powder-in-Tube (PIT) MgB$_2$ coils. The coils properties were measured by transport and magnetization at different applied fields ($H$) and temperatures ($T$). The…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
The paper presents discussion on up to date results on MgB2 conductors from the point of view of their future dc and ac applications. Basic physical parameters of MgB2 compound relevant to conductors are introduced. Different conductor…
Ex-situ Powder-In-Tube MgB2 tapes prepared with ball-milled, undoped powders showed a strong enhancement of the irreversibility field H*, the upper critical field Hc2 and the critical current density Jc(H) together with the suppression of…
We report on the transport, magnetization, and scanning tunneling spectroscopy measurements on c-axis oriented thin films of MgB2 irradiated with high energy heavy ions of uranium and gold. We find a slight shift in the irreversibility and…
The influence of the initial MgB2 grain size on critical current density, upper critical fields and irreversibility has been studied on Fe sheathed monofilamentary MgB2 tapes prepared by the Powder-In-Tube technique. The effect of the…
We have determined the structural properties of the superconducting compound MgB2 as a function of temperature from 11 K to 297 K and as a function of hydrostatic pressure up to 0.62 GPa using neutron powder diffraction. This compound, when…
The anisotropy of the critical current density (Jc) and its influence on measurement of irreversibility field (Birr) has been investigated for high quality, in-situ MgB2 strands. Comparison of transport and magnetization measurements has…
We report the effect of the sintering temperature on the superconductivity of MgB2 pellets prepared under a high pressure of 3 GPa. The superconducting properties of the non-heated MgB2 in this high pressure were poor. However, as the…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
The existence of two phases within one and the same hexagonal lattice of MgB2 compound, differing in Mg and B (in the homogeneity region) and especially in impurity oxygen content, as well as in microstructure, is demonstrated by various…
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…
Studies on the new MgB2 superconductor, with a critical temperature Tc ~ 39 K, have evidenced its potential for applications although intense magnetic relaxation effects limit the critical current density, Jc, at high magnetic fields. This…
Single crystals of MgB2 have been grown with a high-pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB9 ternary nitride. The crystals are of a size up to 2x1x0.1mm3 with a weight up to 230 micrograms.…
We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…