Related papers: Synthesis and Properties of YbB2
A new ternary intermetallic compound, namely, YbMn2Sb2, has been synthesized and its magnetic and electrical transport properties have been studied in the temperature range of 2 to 300 K. This compound crystallizes in a trigonal, La2O2S…
We have synthesized single crystals of Yb$_{2}$Pt$_{2}$Pb, which crystallize in the layered U$_{2}$Pt$_{2}$Sn-type structure, where planes of Yb ions lie on a triangular network. We report here the first results of magnetization, specific…
Ytterbium (Yb) metal is divalent and nonmagnetic but would be expected under sufficient pressure to become trivalent and magnetic. We have carried out electrical resistivity and ac magnetic susceptibility measurements on Yb to pressures as…
Neutron diffraction measurements were carried out on single crystals and powders of Yb2Pt2Pb, where Yb moments form planes of orthogonal dimers in the frustrated Shastry-Sutherland Lattice (SSL). Yb2Pt2Pb orders antiferromagnetically at…
We report magnetization and specific heat measurements down to 2 K and electrical resistivity down to millikelvin temperatures on polycrystalline samples of the non-centrosymmetric compound Yb2Co12P7. In addition to the previously reported…
We report the effect of the sintering temperature on the superconductivity of MgB2 pellets prepared under a high pressure of 3 GPa. The superconducting properties of the non-heated MgB2 in this high pressure were poor. However, as the…
Here, we study YbI$_3$, a quasi-2D layered material with Yb atoms arranged on an ideal honeycomb network of edge-sharing YbI$_6$ octahedra, analogous to the low-temperature phase of $\alpha-$RuCl$_3$. High quality single crystals of YbI$_3$…
We demonstrate from detailed ac-susceptibility and calorimetry studies under hydrostatic pressure that YbCu2Si2 probably orders ferromagnetically at high pressure. The (p,H,T) phase diagram, shows that the transition temperature increases…
Single-phase samples of Yb4LiGe4 and Yb5Ge4 were synthesized using high frequency (HF) heat treatment. Yb4LiGe4 crystallizes in orthorhombic space group Pnma with the Gd5Si4 type of crystal structure and lattice parameters a = 7.0571(1)…
Given the parallelism between the physical properties of Ce and Yb based magnets and heavy fermions due to the electron-hole symmetry, it has been rather odd that the transition temperature of the Yb based compounds is normally very small,…
Measurements of the electric resistivity $\rho(T)$ under pressure up to 8 GPa were performed on high-quality single-crystals of the Yb-based heavy fermion system $\beta$-YbAlB$_4$ in the temperature range $2<T<$ 300 K. In the resistivity…
We report the synthesis and basic properties of single crystals of a new binary compound, Yb$_{3}$Pt$_{4}$. The Yb ions in this compound are fully trivalent, and heat capacity measurements show that the crystal field scheme involves a…
Yb$_2$Si$_2$Al may be a prototype for exploring different aspects of the Shastry-Sutherland lattice, formed by planes of orthogonally coupled Yb ions. Measurements of the magnetic susceptibility find incoherently fluctuating Yb$^{3+}$…
The magnetic ordering of the hexagonal multiferroic compound YbMnO$_3$ has been studied between 100 K and 1.5 K by combining neutron powder diffraction, $^{170}$Yb M\"ossbauer spectroscopy and magnetization measurements. The Yb moments of…
The electric resistivity $\rho(T)$ under hydrostatic pressure up to 8 GPa was measured above 2 K using a high-quality single crystal of the Yb-based heavy fermion system $\beta$-YbAlB$_4$. We found pressure-induced magnetic ordering above…
Low-temperature specific heat and its field-dependence up to 16 T was measured in a stoichiometric single crystal of YbP. A sharp peak was observed at {\it T}$_{\rm N}$ = 0.53 K in zero magnetic field. Application of external field seems to…
The pressure-temperature phase diagram of an intermediate-valence compound YbPd was revealed via simultaneous ac-calorimetry and electrical resistivity measurements. Two successive structural phase transition temperatures, $T_1$ = 125 K and…
We have used neutron diffraction measurements to study the zero-field magnetic structure of the intermetallic compound Yb3Pt4, which was earlier found to order antiferromagnetically at the Neel temperature TN=2.4 K, and displays a…
We report the first study of electrical resistivity, magnetization, and specific heat on YbCo$_2$. The measurements on a single-phased sample of YbCo$_2$ bring no evidence of magnetic ordering down to 0.3 K in a zero magnetic field. The…
Uranium compounds can manifest a wide range of fascinating many-body phenomena, and are often thought to be poised at a crossover between localized and itinerant regimes for 5f electrons. The antiferromagnetic dipnictide USb2 has been of…