We have fabricated a series of iron-sheathed superconducting wires prepared by the powder-in-tube technique from (MgB_2)_{1-x}:(Mg+2B)_x initial powder mixtures taken with different proportions, so that x varies from 0 to 1. It turned out…
Critical current density was measured at 4.2 K for MgB2 strands with and without SiC additions. In some cases measurements were performed on longer (1 m) samples wound on barrels, and these were compared to magnetic measurements. Most…
Hot Isostatic Pressing was applied to synthesize bulk samples with diameter up to 30 mm starting with Alfa Aesar magnesium diboride powder. HIPing at 2 kbar, 1000 C with cooling under pressure (DMCUP cycle) resulted in a fully dense (or low…
Our Rutherford backscattering spectrometry (RBS) study has found that concentrations up to 7 atomic percent of Rb and Cs can be introduced to a depth of ~700 A in MgB2 thin films by annealing in quartz ampoules containing elemental alkali…
The high transition temperature and low surface resistance of MgB2 attracts interest in its potential application in superconducting radio frequency accelerating cavities. However, compared to traditional Nb cavities, the viability of MgB2…
This review article describes the developments over the last 30 months in the thin film growth and junction fabrication of superconducting MgB2, including a brief summary the chemistry and physics of MgB2.
The MgB2 superconductor has already demonstrated its applicative potential, in particular for DC applications such as MRI magnets, thanks to the low costs of the raw materials and to its simple production process. However further efforts…
Neutron powder diffraction has been used to characterize a sample of C-substituted MgB2 synthesized from Mg and B4C (with isotopically enriched 11B). The sample is multiphase, with the major phase [73.4(1) wt.%] being Mg(B1-xCx)2 with…
We report variation of lattice structure in diborides (AB2) with different A atoms to identify the special case of MgB2 showing high Tc superconductivity. High purity MgB2 (Tc~39 K) has been prepared by direct reaction of the elements and…
We present a new method to synthesize bulk indium nitride by means of a simple solid-state chemical reaction carried out under hydrostatic high pressure/high temperature conditions in a multi-anvil apparatus, not involving gases or solvents…
Magnesium diboride (MgB2) powder was mechanically alloyed by high energy ball milling with C to a composition of Mg(B0.95C0.05)2 and then sintered at 1000 C in a hot isostatic press. Milling times varied from 1 minute to 3000 minutes. Full…
An advanced internal Mg infiltration method (AIMI) in this paper has been shown to be effective in producing superconducting wires containing dense MgB2 layers with high critical current densities. In this study, the in-field critical…
We present a modified method of preparation of the new superconductor MgB$_2$. The polycrystalline samples were characterized using x-ray and magnetic measurements. The surface barriers control the isothermal magnetization loops in powder…
Magneto-optical imaging was used to study a zero-field-cooled MgB2 film at 9.6K where in a slowly increasing field the flux penetrates by abrupt formation of large dendritic structures. Simultaneously, a gradual flux penetration takes…
We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The…
Processing methods are described for the development of magnesium diboride wire using the chemical vapor deposition (CVD) to produce long lengths of suitably doped starting boron fiber. It is found that titanium can be co-deposited with the…
0.5 to 5.0 wt.% Dy2O3 was in-situ reacted with Mg + B to form pinned MgB2. While Tc remained largely unchanged, Jc was strongly enhanced. The best sample (only 0.5 wt.% Dy2O3) had a Jc of 6.5 x 10^5 A/cm^2 at 6K, 1T and 3.5 x 10^5 A/cm^2 at…
Superconducting thin films have been prepared on Si-substrates, using pulsed laser deposition from a target composed of a mixture of Mg and MgB2 powders. The films were deposited at room temperature and post-annealed at 600 degrees C. The…
We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…
The hydrostatic pressure effect on the newly discovered superconductor MgB2 has been determined. The transition temperature Tc was found to decrease linearly at a large rate of -1.6 K/GPa, in good quantitative agreement with the ensuing…