The superconducting transition temperature, T$_{C}$, the residual resistivity $\rho_{0}$ and the slope of resistivity curve at high temperature, d$\rho$/dT, have been measured in a series of MgB$_{2}$ samples that have been chemically…
The variation of TC in MgB2 has been systematically investigated for monovalent cation substitution in Mg1-xLixB2 and in Mg1-xCuxB2 and simultaneous cation and Carbon substitution in Mg0.80Li0.20B2-xCx and Mg0.95Cu0.05B2-xCx using dc…
Growth of carbon substituted magnesium diboride Mg(B1-xCx)2 single crystals with 0<x<0.15 is reported and the structural, transport, and magnetization data are presented. The superconducting transition temperature decreases monotonically…
We report that the ternary MgB2-xCx compounds adopt an isostructural AlB2-type hexagonal structure in a relatively small range of nominal carbon concentration, x<0.1. The lattice parameter a decreases almost linearly with increasing carbon…
Carbon-substituted MgB2 single crystals, Mg(B_1-xC_x)_2 of 0.3-1.0 mm size were grown for x=0.02-0.15 by a high-pressure technique. The doping dependence of lattice constants studied in a range of x=0.0-0.2 shows a monotonic decrease in a,…
The DC magnetization and AC complex magnetic susceptibilities were measured for MgB2 single crystals, unsubstituted and carbon substituted with the composition of Mg(B_0.94C_0.06)2. The measurements were performed in AC and DC magnetic…
A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
Effects of magnetic impurity on the superconductivity has been investigated in Mg1-xMnB2. With increase of Mn concentration x, the lattice constant c (perpendicular to the boron sheet) decreases at a rate of -1.4 % (= dlnc/dx), while a…
We prepared MgB$_{2-x}$Be$_{x}$ ($x=0$, 0.2, 0.3, 0.4, and 0.6) samples where B is substituted with Be. MgB$_{2}$ structure is maintained up to $x=0.6$. In-plane and inter-plane lattice constants were found to decrease and increase,…
The change in the lattice parameters or the lattice disorder is claimed as a cause of the slight reduction in the transition temperature by carbon doping in MgB2. In this work, an extensive investigation on the effects of carbohydrate…
We report the synthesis, magnetic susceptibility and crystal structure analysis for NbB2+x (x = 0.0 to 1.0) samples. The study facilitates in finding a correlation among the lattice parameters, chemical composition and the superconducting…
The recent discovery of superconductivity at ~39 K in MgB2, by Nagamatsu et al. establishes this simple binary compound as having the highest bulk superconducting transition temperature, Tc, of any non-copper-oxide material. Much of the…
Superconductivity is observed with critical temperature $T_{c}$ = 2.0 K in self-flux-grown single crystals of $CaBi_{2}$. This material adopts the $ZrSi_{2}$ structure type with lattice parameters a = 4.696(1) $\AA$, b = 7.081(2) $\AA$ and…
A detailed investigation of the series CuCr(1-x)MgxO2 (x = 0.0 - 0.05) has been performed by making high-temperature resistivity and thermopower measurements, and by performing a theoretical analysis of the latter. Microstructure…
Bulk superconducting samples of MgB2 were prepared by solid state reaction of stoichiometric quantities of Mg turnings and B in a sealed Ta cylinder at 890 C for 2 hours. The as-synthesized MgB2 samples had a Tc of 39 K, as defined as the…
We evaluated the doping effects of carbohydrate (malic acid, C4H6O5), from 0wt% to 30wt% of total MgB2, on the phase, lattice parameters, critical temperature, resistivity, and upper critical field of MgB2 superconductor. The lattice…
The hydrostatic pressure effect on the newly discovered superconductor MgB2 has been determined. The transition temperature Tc was found to decrease linearly at a large rate of -1.6 K/GPa, in good quantitative agreement with the ensuing…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
We report $^{11}$B-NMR study on Al-doped MgB$_2$ that addresses a possible mechanism for a high superconducting (SC) transition temperature ($T_c$) of $\sim 40$ K in recently discovered MgB$_2$. The result of nuclear spin lattice relaxation…
We have studied the changes in the electronic structure and the superconducting transition temperature T_c of Mg(B_{1-x}C_{x})_{2} alloys as a function of x with 0\leq x\leq 0.3. Our density-functional-based approach uses coherent-potential…