The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
MgB2-diamond nanocomposite superconductors have been synthesized by addition of nano-diamond powder. Microstructural analysis shows that the nanocomposite superconductor consists of tightly-packed MgB2 nano-grains (~50-100 nm) with…
Polycrystalline MgB2 samples with 10 wt % silicon powder addition were prepared by an in-situ reaction process. Two different Si powders, one with coarse (44 mm) and the other with nano-size (<100 nm) particles were used for making samples.…
Highly dense MgB2 policrystalline bulk materials, obtained by reactive liquid infiltration, have been characterized in their superconducting transport and magnetic properties in magnetic field and in a temperature range of interest for the…
Superconducting properties of bulk, dense, pure MgB2 and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were studied for compositional ranges 0 < x < 0.20. The effect on pinning properties and critical current were…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
We report a significant enhancement of the upper critical field $H_{c2}$ of different $MgB_2$ samples alloyed with nonmagnetic impurities. By studying films and bulk polycrystals with different resistivities $\rho$, we show a clear trend of…
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
Nanocrystalline MgB$_2$ produced by mechanical alloying has been shown to exhibit enhanced superconducting properties such as increased pinning and higher critical currents. However, the effects of the synthesis process on the intrinsic…
Bulk samples of MgB2 were prepared with 5, 10, and 15% wt.% Y2O3 nanoparticles added using a simple solid-state reaction route. Transmission electron microscopy (TEM) showed a fine nanostructure consisting of ~3-5 nm YB4 nanoparticles…
We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of…
This review paper illustrates the main normal and superconducting state properties of magnesium diboride, a material known since early 1950's, but recently discovered to be superconductive at a remarkably high critical temperature Tc=40K…
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
We study the effect of nano(n)-SiC addition on the crystal structure, critical temperature (Tc), critical current density (Jc) and flux pinning in MgB2 superconductor. X-ray diffraction patterns show that all the samples have MgB2 as the…
A MgB2 superconducting tape has been successfully prepared by a new way of boron diffusion into Mg tape. This tape superconductor has a Tc of 39 K with a sharp transition width of 0.4 K, high bulk critical current density jc of 6.7*10^5…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…