Related papers: High current-carrying capability in c-axis-oriente…
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires…
A Hybrid Physical-Chemical Vapour Deposition (HPCVD) system consisting of separately controlled Mg-source heater and substrate heater is used to grow MgB2 thin films and thick films at various temperatures. We are able to grow…
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance…
Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were…
We report on electrical transport properties of epitaxial Ba(Fe1-xNix)2As2 thin films grown by pulsed laser deposition in static magnetic fields up to 35 T. The thin film shows a critical temperature of 17.2 K and a critical current density…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated by transport, ac susceptibility and dc magnetization measurements in magnetic fields up to 16 T covering a temperature…
An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter…
Critical current density Jc in polycrystalline or granular superconducting material is known to be hysteretic with applied field H due to the focusing of field within the boundary between adjacent grains. This is of concern in the so-called…
We report the influence of crystalline defects introduced by 6 MeV $^{16}$O$^{3+}$ irradiation on the critical current densities J$_c$ and flux creep rates in 1.3 $\mu$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductor produced by…
Current-voltage characteristics of top seeded melt-textured YBa2Cu3O7-d are presented. The samples were cut out of centimetric monoliths. Films characteristics were also measured on microbridges patterned on thin films grown by dc…
We reported far-infrared transmission measurements on a c-axis oriented superconducting MgB$_{2}$ thin film in the frequency range of 30 $\sim$ 250 cm$^{-1}$. We found that these measurements were sensitive to values of scattering rate…
MgB2/Fe tapes with 2.5-15 at.% ZrB2 additions were prepared through the in situ powder-in-tube method. Compared to the pure tape, a significant improvement in the in-field critical current density Jc was observed, most notably for 10 at.%…
Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…
We report herein a high and isotropic critical-current density Jc for BaFe2(As,P)2 epitaxial films. The isotropy of Jc with respect to the magnetic-field direction was improved significantly by decreasing the film growth rate to 2.2…
Novel behavior of the critical current density $j_{c}$ of a regularly perforated superconducting film is found, as a function of applied magnetic field $H$. Previously pronounced peaks of $j_{c}$ at matching fields were always found to…
The K- and Co-doped BaFe2As2 (Ba-122) superconducting compounds are potentially useful for applications because they have upper critical fields (Hc2) of well over 50 T, Hc2 anisotropy Gamma < 2, and thin film critical current densities…
MgB2 thin films were deposited using Pulsed Laser Deposition (PLD) and ex-situ annealing in Mg atmosphere. The films presented critical temperatures up to 36K and turned out to be preferentially c-oriented both on Al2O3 (r-cut) and MgO(100)…
The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of…