Related papers: Optical conductivity and penetration depth in MgB2
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
The in-plane optical conductivity of UPd_2Al_3 was measured at temperatures $2 {\rm K}<T<300$ K in the spectral range from 1 cm^{-1} to 40 cm^{-1} (0.14 meV to 5 meV). As the temperature decreases below 25 K a well pronounced pseudogap of…
Polarisation-resolved Raman scattering measurements were performed on MgB_2 single crystals to determine the magnitude, symmetry and temperature dependence of the superconducting gap. A single sharp peak due to Cooper pair breaking appears…
We investigate evolution of the magnetic penetration depth and superconducting energy gap in epitaxial NbN films using a low frequency mutual inductance technique and tunneling spectroscopy using a low temperature scanning tunneling…
The study of the anisotropic superconductor MgB2 using a combination of scanning tunneling microscopy and spectroscopy reveals two distinct energy gaps at Delta1=2.3 meV and Delta2=7.1 meV. Different spectral weights of the partial…
We have performed flux noise and AC-susceptibility measurements on two 400 nm thick MgB$_2$ films. Both measurement techniques give information about the vortex dynamics in the sample, and hence the superconducting transition, and can be…
The low frequency complex impedance of a high resistivity 92 {\mu}{\Omega} cm and 100 nm thick TiN superconducting film has been measured via the transmission of several high sensitivity GHz microresonators, down to Tc/50. The temperature…
The recently-discovered MgB2 super-conductor has a transition temperature Tc approaching 40K, placing it intermediate between the families of low and high temperature super-conductors (LTS and HTS). In practical applications,…
We report on the temperature-dependent optical response of thin films of YBa2Cu3O7-{\delta} (YBCO) in the visible spectral range under cryogenic conditions. Specifically, we observe an increase in transmittance near the superconducting…
Composites consisting of MgB2 and Al, 11% by volume, undergo a transition to superconductivity onset at TC = 38 K, close to the value reported for pure MgB2. The transition appears to have broadened, as determined by both magnetic and…
We report on measurements of the specific heat of the recently discovered superconductor MgB$_2$ in the temperature range between 3 and 220 K. Based on a modified Debye-Einstein model, we have achieved a rather accurate account of the…
The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron…
Solid MgB$_2$ has rather interesting and technologically important properties, such as a very high superconducting transition temperature. Focusing on this compound, we report the first non-trivial application of a novel…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
High quality, ultrathin, superconducting films are required for advanced devices such as hot-electron bolometers, superconducting nanowire single photon detectors, and quantum applications. Using Hybrid Physical-Chemical Vapor Deposition…
We have measured the temperature dependence of the microwave surface impedance Zs = Rs + i\Omega\mu_0 \Lamda of two c-axis oriented MgB2 films at a frequency \Omega /(2\pi) of 17.9 GHz employing a dielectric (sapphire) resonator technique.…
The effective superconducting penetration depth measured in the vortex state of PrOs4Sb12 using transverse-field muon spin rotation (TF-muSR) exhibits an activated temperature dependence at low temperatures, consistent with a nonzero gap…
Starting from first principles, we show the formation and evolution of superconducting gaps in MgB$_2$ at its ultrathin limit. Atomically thin MgB$_2$ is distinctly different from bulk MgB$_2$ in that surface states become comparable in…
Thin films of $\alpha$-MoGe show progressively reduced $T_{c}$'s as the thickness is decreased below 30 nm and the sheet resistance exceeds 100 $\Omega/\Box$. We have performed far-infrared transmission and reflection measurements for a set…
We have successfully synthesized MgB2 thick films on 4H-SiC substrate by hybrid physical-chemical deposition (HPCVD). The films have transition temperature TC above 40 K. X-ray diffraction (XRD) shows the c-axis oriented structure of MgB2,…