We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…
Cryogenic scanning tunneling microscopy and magnetization measurements were used to study the superconducting properties of MgB_2. The magnetization measurements show a sharp superconductor transition onset at T_c = 38.5 K, in agreement…
Using mm-wave transmission we obtain information about both the real and imaginary part of the dielectric function of superconducting thin films. This is done by fitting the Fabry-Perot resonance spectrum for the film plus substrate over a…
We reported far-infrared transmission measurements on a c-axis oriented superconducting MgB$_{2}$ thin film in the frequency range of 30 $\sim$ 250 cm$^{-1}$. We found that these measurements were sensitive to values of scattering rate…
We report the temperature dependent magnetic penetration depth $\lambda(T)$ and the superconducting critical field $H_{c2}(T)$ in a 500-nm MgB$_{2}$ film. Our analysis of the experimental results takes into account the two gap nature of the…
We study the new binary intermetallic superconductor MgB2 using high-resolution photo-emission spectroscopy. The superconducting-state spectrum measured at 5.4 K shows a coherent peak with a shoulder structure, in sharp contrast to that…
The temperature-dependent optical reflectivity and complex transmissivity of an epitaxially grown Ba(Fe$_{0.9}$Co$_{0.1}$)$_2$As$_2$ thin film were measured and the optical conductivity and permittivity evaluated over a wide frequency…
We measured the in-plane optical conductivity of a nearly optimally doped (Ba,K)Fe2As2 single crystal with Tc = 39.1 K. Upon entering the superconducting state the optical conductivity below ~20 meV vanishes, strongly suggesting a fully…
The specific heat of two polycrystalline samples of MgB_2 is presented and analyzed (2 - 300 K, 0 - 16 T), together with magnetic properties. The main characteristics are a low density of states at the Fermi level, high phonon frequencies,…
Surface impedance measurements of LuNi2B2C superconducting thin films as a function of temperature have been performed down to 1.5 K and at 20 GHz using a dielectric resonator technique. The magnetic penetration depth closely reproduces the…
We present a high-resolution microwave spectrometer to measure the frequency-dependent complex conductivity of a superconducting thin film near the critical temperature. The instrument is based on a broadband measurement of the complex…
Here we report an optical investigation in the terahertz region of a 40 nm ultrathin BaFe$_{1.84}$Co$_{0.16}$As$_2$ superconducting film with superconducting transition temperature T$_c$ = 17.5 K. A detailed analysis of the combined…
MgB2 superconducting wires with critical temperature Tc approaching 40 K were used for preparation of MgB2/Ag and MgB2/In junctions. The differential conductance vs. voltage characteristics of N-S junctions exhibit clear contribution of…
The optical conductivity of MgB$_2$ has been determined on a dense polycrystalline sample in the spectral range 6 meV - 4.6 eV using a combination of ellipsometric and normal incidence reflectivity measurements. $\sigma_{1}(\omega)$…
A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
Superconductivity is observed with critical temperatures near 9K in the tetragonal compound Mo5PB2. This material adopts the Cr5B3 structure type common to supercondcuting Nb5Si3-xBx, Mo5SiB2, and W5SiB2, which have critical temperatures of…
Infrared absorption measurements in the range of 125 to 700 cm^(-1) have been carried out as a function of temperature upto 5 K in MgB2. The absorption spectrum is characterised by a broad band centred at 485 cm^{-1}, with shoulders at 333…
Upper critical fields of four MgB2 thin films were measured up to 28 Tesla at Grenoble High Magnetic Field Laboratory. The films were grown by Pulsed Laser Deposition and showed critical temperatures ranging between 29.5 and 38.8 K and…
Heat-capacity measurements of a 39 microgramm MgB_2 single crystal in fields up to 14 T and below 3 K allow the determination of the low-temperature linear term of the specific heat, its field dependence and its anisotropy. Our results are…
We report scanning tunneling spectroscopy (STS) measurements of the gap properties of both ceramic MgB2 and c-axis oriented epitaxial MgB2 thin films. Both show a temperature dependent zero bias conductance peak and evidence for two…