The effects of Mg deficiency in MgB2 films grown by using hybrid physical-chemical vapor deposition were investigated after vacuum annealing at various temperatures. High-quality MgB2 films grown on c-cut Al2O3 substrates with different…
We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…
Low resistivity (~3-24 mOhm.cm) with tunable n- and p-type phase pure Cu2O thin films have been grown by pulsed laser deposition at 25-200 0C by varying the background oxygen partial pressure (O2pp). Capacitance data obtained by…
Micron-thick boron films have been deposited by Pulsed Laser Deposition in vacuum on several substrates at room temperature. The use of high energy pulses (>700 mJ) results in the deposition of smooth coatings with low oxygen uptake even at…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
We have grown Au/Ag modulated nanostructured thin films by pulsed laser deposition using metallic targets. The growths performed at room temperature involved deposition of alternate layers of the two metals with larger thickness of Au and…
A Hybrid Physical-Chemical Vapour Deposition (HPCVD) system consisting of separately controlled Mg-source heater and substrate heater is used to grow MgB2 thin films and thick films at various temperatures. We are able to grow…
The influence of SiC-impurity layer and growth temperature on microstructure and superconducting properties were studied for MgB2 superconducting tapes. The pulsed laser deposition (PLD) system was used for the deposition of amorphous…
We introduce a simple method of an MgB2 film preparation using sequential electron-beam evaporation of B-Mg two-layer (followed by in-situ annealing) on the NbN buffered Si(100) substrate. The Transmission Electron Microscopy analyses…
We report the growth of highly c-axis oriented topological insulator (TI) BiSbTe1.5Se1.5 (BSTS) thin films by pulsed laser deposition (PLD) technique. The various growth parameters such as substrate temperature, Argon pressure in the…
In this paper we report a new sol-gel method for the fabrication of MgB2 films. Polycrystalline MgB2 films were prepared by spin-coating a precursor solution of Mg(BH_4)_2 diethyl ether on (001)Al2O3 substrates followed with annealing in Mg…
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…
Ultrathin MgB2 superconducting films with a thickness down to 7.5 nm are epitaxially grown on (0001) Al2O3 substrate by hybrid physical-chemical vapor deposition method. The films are phase-pure, oxidation-free and continuous. The 7.5 nm…
Biaxially textured LuNi2BC thin films with Tc up to 15.8 K and a residual resistivity ratio up to 15 have been prepared. The films were deposited on MgO(110) substrates using pulsed laser deposition from a stoichiometric target. Via the…
Superconducting thin films of magnesium diboride (MgB$_2$) were prepared on MgO (001) substrate by a molecular beam epitaxy (MBE) method with the co-evaporation conditions of low deposition rate in ultra-high vacuum. The structural and…
The remarkably high superconducting transition temperature and upper critical field of iron(Fe)-based layered superconductors, despite ferromagnetic material base, open the prospect for superconducting electronics. However, success in…
As-grown superconducting thin films of MgB2 were prepared by molecular beam epitaxy (MBE), and studied by X-ray and ultraviolet photoelectron spectroscopy (XPS and UPS). Only films prepared at temperatures between 150 and 320 deg. showed…
The discovery of superconductivity at 39 K in magnesium diboride offers the possibility of a new class of low-cost, high-performance superconducting materials for magnets and electronic applications. With twice the critical temperature of…
ctical superconducting material for power-electric products such as superconducing tapes because of its high superconducting transition temperature (Tc) of 39 K and its high critical current density (Jc) under magnetic fields.…
Epitaxial titanium diboride thin films have been deposited on sapphire substrates by Pulsed Laser Ablation technique. Structural properties of the films have been studied during the growth by Reflection High Energy Electron Diffraction…