Related papers: Microwave properties of superconducting $MgB_{2}$
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
Materials of the Y-Ba-Cu-O (melt-textured YBa2Cu3O7-d-based materials or MT-YBCO) and Mg-B-O (MgB2-based materials) systems with high superconducting performance, which can be attained due to the formation of regularly distributed…
The cusp-like behavior of the microwave conductivity observed in clean ortho-II YB$_{2}$Cu$_{3}$O$_{6.50}$ at low temperature and low frequency is shown to be related directly to a linear in frequency dependence of the impurity scattering…
Continuous Nb wires, 7-15 nm in diameter, have been fabricated by sputter-coating single fluorinated carbon nanotubes. Transmission electron microscopy revealed that the wires are polycrystalline, having grain sizes of about 5 nm. The…
We give a broad overview of the history of microwave superconductivity and explore the technological developments that have followed from the unique electrodynamic properties of superconductors. Their low loss properties enable resonators…
The discovery of superconductor in magnesium diboride MgB2 with high Tc (39 K) has raised some challenging issues; whether this new superconductor resembles a high temperature cuprate superconductor(HTS) or a low temperature metallic…
The results of electrical resistance (1.4 - 300 K), magnetization (2-300 K) and heat-capacity (2 - 50 K) measurements in Y$_2$PdGe$_3$, found to crystallize in a AlB$_2$-derived hexagonalstructure, are reported. The results establish that…
Systematic microwave surface impedance measurements of YBCO single crystals grown in $BaZrO_3$ crucibles reveal new properties that are not directly seen in similar measurements of other YBCO samples. Two key observations obtained from…
The electronic properties of superconducting Sn films ($T_c \approx$ 3.8 K) change significantly when reducing the film thickness down to a few nm, in particular close to the percolation threshold. The low-energy electrodynamics of such Sn…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
We report measurements of the surface impedance $Z_s=R_s+iX_s$ of $(Pr_xY_{1-x})Ba_2Cu_3O_{7-\delta}$, $(x=0,0.15,0.23,0.3,0.4,0.5)$. Increasing $Pr$ concentration leads to some striking results not observed in samples doped by non-magnetic…
160 MeV Neon ion irradiation has been carried out on MgB2 polycrystalline pellets at various doses. There has not been any significant change in Tc except at the highest dose of 1x10^15 ions/cm^2. Increase in resistivity has been noticed.…
We present a microwave characterization of a DyBa$_{2}$Cu$_{3}$O$_{7-x}$ single domain, grown by the top-seeded melt-textured technique. We report the (a,b) plane field-induced surface resistance, $\Delta R_s(H)$, at 48.3 GHz, measured by…
The optical conductivity of MgB$_2$ has been determined on a dense polycrystalline sample in the spectral range 6 meV - 4.6 eV using a combination of ellipsometric and normal incidence reflectivity measurements. $\sigma_{1}(\omega)$…
The lower critical field $H_{c1}$ has been carefully measured on a well shaped cylindrical sample of the new superconductor $MgB_2$ fabricated by high pressure synthesis. The penetration depth $\lambda$ is calculated from the $H_{c1}$ data.…
In order to understand the unexpected superconducting behavior of MgB$_2$ compound we have made electronic structure calculations for MgB$_2$ and closely related systems. Our calculated Debye temperature from the elastic properties indicate…
Results of X-band microwave surface impedance measurements of FeSe1-xTex very thin film are reported. The effective surface resistance shows appearance of peak at T less and near Tc when plotted as function of temperature. The authors…
Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin…
We have performed susceptibility, thermopower, dc resistance and microwave measurements on RuSr2EuCu2O8. This compound has recently been shown to display the coexistence of both superconducting and magnetic order. We find clear evidence of…
The microwave properties of polycrystalline MgB2 thin films prepared by the so-called in-situ method are investigated. The characterization of the films at microwave frequencies was obtained by a coplanar resonator technique. The analysis…