We prepared MgB$_{2-x}$Be$_{x}$ ($x=0$, 0.2, 0.3, 0.4, and 0.6) samples where B is substituted with Be. MgB$_{2}$ structure is maintained up to $x=0.6$. In-plane and inter-plane lattice constants were found to decrease and increase,…
The effect of Li substitution for Mg and of Li-C co-substitution on the superconducting properties and crystal structure of MgB2 single crystals has been investigated. It has been found that hole doping with Li decreases the superconducting…
In this paper, we reported the structural properties and superconductivity of Mg(B1-xCx)2 compounds. Powder x-ray diffraction results indicate that the samples crystallize in a hexagonal AlB2-type structure. Due to the chemical activity of…
The superconducting and structural properties of a series of Mg1-xAlxB2 samples have been investigated. X-ray diffraction results confirmed the existence of a structural transition associated with the significant change in inter-boron layer…
Effect of Ti doping on the electrical transport and magnetic properties of layered Na0.8Co1-xTixO2 compounds has been investigated. The lattice parameters a and c increase with x. A minor amount of Ti doping results in a metal-insulator…
The effect of nano-C doping on the microstructure and superconducting properties of Fe-sheathed MgB2 tapes prepared through the in-situ powder-in-tube method was studied. Heat treatment was performed at a low temperature of 650C for 1 h.…
We report the preparation of Mg$_{1-x}$B$_{2}$ (0$\le$x$\le$0.5) compounds with the nominal compositions. Single phase MgB$_{2}$ was obtained for x=0 sample. For 0$<$x$\le$0.5, MgB$_{4}$ coexists with "MgB$_{2}$" and the amount of MgB$_{4}$…
The change in the lattice parameters or the lattice disorder is claimed as a cause of the slight reduction in the transition temperature by carbon doping in MgB2. In this work, an extensive investigation on the effects of carbohydrate…
We prepared a series of Mg_{1-x}(AlLi)_{x}B_2 samples with 0≤x≤0.45 in order to compensate with Li the electron doping induced by Al. Structural characterization by means of neutron and X-ray diffraction confirms that Li enters…
The superconductivity in Na0.3Co1-xMxO2.1.3H2O and the charge ordering in Na0.5Co1-xMxO2 have been investigated for M = Mn and Ti substituting for Co. We have first successfully synthesized the single-phase Na0.7Co1-xMxO2(M= Mn and Ti)…
The physical property characterization of Al doped Mg1-xAlxB2 system with x = 0.0 to 0.50 is reported. The results related to phase formation, structural transition, resistivity R(T) and magnetization M(T) measurements are discussed in…
The variation of TC in MgB2 has been systematically investigated for monovalent cation substitution in Mg1-xLixB2 and in Mg1-xCuxB2 and simultaneous cation and Carbon substitution in Mg0.80Li0.20B2-xCx and Mg0.95Cu0.05B2-xCx using dc…
We report that the ternary MgB2-xCx compounds adopt an isostructural AlB2-type hexagonal structure in a relatively small range of nominal carbon concentration, x<0.1. The lattice parameter a decreases almost linearly with increasing carbon…
Effects of magnetic impurity on the superconductivity has been investigated in Mg1-xMnB2. With increase of Mn concentration x, the lattice constant c (perpendicular to the boron sheet) decreases at a rate of -1.4 % (= dlnc/dx), while a…
By using solid state reaction method we have fabricated the hole doped $La_{1-x}Sr_xFeAsO$ superconductors with Sr content up to 0.13. It is found that the sharp anomaly at about 150 K and the low temperature upturn of resistivity are…
A comprehensive study of the effects of carbohydrate doping on the superconductivity of MgB2 has been conducted. In accordance with the dual reaction model, more carbon substitution is achieved at lower sintering temperature. As the…
We report measurements on MgB2 up to ~40GPa. Increasing pressure yields a monotonous decrease of the lattice parameters and of the c/a ratio, but no structural transition down to parameters smaller than those of AlB2. The transition…
We have determined the structural properties of the superconducting compound MgB2 as a function of temperature from 11 K to 297 K and as a function of hydrostatic pressure up to 0.62 GPa using neutron powder diffraction. This compound, when…
The effects of simultaneous Sb doping on the superconductivity of 112-type Ca1-xRExFeAs2 (RE = La, Ce, Pr, and Nd) were studied through measurements of the magnetization and electrical resistivity. In Sb-free materials, the superconducting…
LiB, a predicted layered compound analogous to the MgB$_2$ superconductor, has been recently synthesized via cold compression and quenched to ambient pressure, yet its superconducting properties have not been measured. According to prior…