Related papers: Superconductivity in Dense $MgB_2$ Wires
A superconductor is a material that can conduct electricity with no resistance below its critical temperature (Tc). The highest Tc that has been achieved in cuprates1 is 133 K at ambient pressure2 and 164 K at high pressures3. As the nature…
Materials of the Y-Ba-Cu-O (melt-textured YBa2Cu3O7-d-based materials or MT-YBCO) and Mg-B-O (MgB2-based materials) systems with high superconducting performance, which can be attained due to the formation of regularly distributed…
We report on the synthesis and the physical properties of Ba1-xRbxTi2Sb2O (x < 0.4) by x-ray diffraction, SQUID magnetometery, resistivity and specific heat measurements. Upon hole doping by substituting Ba with Rb, we find…
The MgB2 superconductor has already demonstrated its applicative potential, in particular for DC applications such as MRI magnets, thanks to the low costs of the raw materials and to its simple production process. However further efforts…
Cryogenic scanning tunneling microscopy and magnetization measurements were used to study the superconducting properties of MgB_2. The magnetization measurements show a sharp superconductor transition onset at T_c = 38.5 K, in agreement…
Since the discovery of superconductivity in MgB2 considerable progress has been made in determining the physical properties of the material, which are promising for bulk conductors. Tunneling studies show that the material is reasonably…
The influence of the nature of the boron precursor on the superconducting properties of polycrystalline MgB2 was studied. Critical current densities for the MgB2 made from high purity amorphous boron are at least a factor of three higher…
We demonstrate that good superconductor/insulator/normal-metal tunnel junctions can be fabricated on as-grown superconducting MgB2 thin films. The as-grown films were prepared by coevaporation at low growth temperatures of around 280deg.…
We have studied the evolution of superconducting and normal state properties of neutron irradiated Mg(B$_{.962}$C$_{.038}$)$_2$ wire segments as a function of post exposure annealing time and temperature. The initial fluence fully…
WBe2, which occurs in space group 194, with hexagonal symmetry P63/mmc, is prepared by arc-melting at temperatures above 2200 C, where Be vapor loss is significant. This study is motivated by recent work on MoB2 and WB2, both…
We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of…
Electrolysis has been performed on a fused mixture of magnesium chloride, potassium chloride, and magnesium borate at 600 oC under an Ar atmosphere using a graphite anode and a Pt cathode. Magnetic measurements and X-ray diffractometry have…
The transport properties of superconducting single crystal Pb nanowires of 55 nm and 70 nm diameter are studied by standard four electrodes method. Resistance-temperature (R-T) scans and magneto-resistance (R-H) measurements show a series…
Magnesium diboride has been thermally treated in the presence of Rb, Cs, and Ba. Magnetic susceptibility shows onsets of superconductivity in the resulting samples at 52K (Rb), 58K (Cs) and 45K (Ba). Room-temperature 11B NMR indicates to…
Superconductivity is observed with critical temperatures near 9K in the tetragonal compound Mo5PB2. This material adopts the Cr5B3 structure type common to supercondcuting Nb5Si3-xBx, Mo5SiB2, and W5SiB2, which have critical temperatures of…
The powder in tube method has been used to fabricate Ag and Cu clad MgB2 wires using an in-situ reaction method. The effects of short time sintering on the critical current densities of Ag and Cu clad MgB2 wires were studied. All the…
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical…
Transport critical current (Ic) was measured for MgB2/Fe round wires, with magnetic field oriented perpendicular to the wire and parallel to it. Measurements were made on a wire with pure MgB2 core and another wire where MgB2 core was doped…
We have fabricated and characterized samples of the superconducting- semiconducting Bi-Pb-Sb-Sr-Ca-Cu-O/CdS composite. Nano-size particles of CdS were deposited and introduced into the porosities of the Bi-Pb-Sb-Sr-Ca-Cu-O material by the…
We report on syntheses and electron transport properties of polycrystalline samples of diborides (AB2) with different transition metals atoms (A=Zr,Nb,Ta). The temperature dependence of resistivity, \rho(T), and ac susceptibility of these…