Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…
We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…
We report variation of lattice structure in diborides (AB2) with different A atoms to identify the special case of MgB2 showing high Tc superconductivity. High purity MgB2 (Tc~39 K) has been prepared by direct reaction of the elements and…
The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD…
MgB2 is a promising superconductor for important large-scale applications for both high field magnets and cryocooler-cooled magnet operated at temperatures around 20 K. In this work, by utilizing C60 as a viable alternative dopant, we…
The results of electrical resistance (1.4 - 300 K), magnetization (2-300 K) and heat-capacity (2 - 50 K) measurements in Y$_2$PdGe$_3$, found to crystallize in a AlB$_2$-derived hexagonalstructure, are reported. The results establish that…
Superconducting MgB2 was synthesized in a stainless steel tube which compressed by pulsed magnetic field. The temperature dependence of diamagnetic moment m(T) was investigated and the pinning potential was determined
Nb-sheathed Sr0.6K0.4Fe2As2 superconducting wires have been fabricated using the powder-in-tube (PIT) method for the first time and the superconducting properties of the wires have been investigated. The transition temperature (Tc) of the…
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in…
We have measured the Raman spectra of polycrystalline MgB$_{2}$ from 25 {\cm} to 1200 {\cm}. When the temperature was decreased below the superconducting transition temperature $T_c$, we observed a superconductivity-induced redistribution…
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS).…
In this paper we report a new synthesis route to produce boron powders characterized as being amorphous and having very fine particle size. This route has been developed to improve the performances of superconducting MgB2 powders, which can…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
We have observed the conduction electron spin resonance (CESR) in fine powders of MgB2 both in the superconducting and normal states. The Pauli susceptibility is chi_s=2.0*10^{-5} emu/mole in the temperature range of 450 to 600 K. The spin…
We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…
The search for superconductivity in materials iso-structural and iso-valent with magnesium diboride, MgB2, has not yielded any results close enough to the 39K Tc of MgB2. Lithium magnesium nitride, LiMgN, resembles MgB2 in that they both…
Conventional electron beam lithography has been used to fabricate mesoscopic Nb wires with a superconducting transition temperature above 7.0 K. The typical line width and the thickness were 200 nm and 45 nm respectively. Nb was deposited…
Last year, iron was reported to become superconducting at temperatures below 2K and pressures between 15 and 30 GPa. The evidence presented was a weak resistivity drop, suppressed by a magnetic field above 0.2 T, and a small Meissner…
Measurements of the penetration depth $\lambda (T,H)$ in the presence of a DC magnetic field were performed in $MgB_2$ wires. In as-prepared wires $\lambda (T,H<130 Oe)$ shows a strong diamagnetic downturn below $\approx 10 K$. A DC…
Nanocrystalline MgB$_2$ produced by mechanical alloying has been shown to exhibit enhanced superconducting properties such as increased pinning and higher critical currents. However, the effects of the synthesis process on the intrinsic…