Related papers: Superconductivity in Dense $MgB_2$ Wires
MgB2 hollow wires have been produced with a new technique which uses a conventional wire manufacturing process but is applied to composite billets containing the elemental B and Mg precursors in an appropriate shape. The technique has been…
Sintered powders and wires of superconducting $MgB_2$ have been fabricated under a variety of conditions in order to determine details of the diffusion of the $Mg$ into $B$ and to study the types of defects that arise during growth. For…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
A MgB2 superconducting tape has been successfully prepared by a new way of boron diffusion into Mg tape. This tape superconductor has a Tc of 39 K with a sharp transition width of 0.4 K, high bulk critical current density jc of 6.7*10^5…
Measurements of the $10GHz$ microwave surface resistance of dense $MgB_{2}$ wire and pellet are reported. Significant improvements are observed in the wire with reduction of porosity. The data lie substantially above the theoretical…
Porous magnesium diboride samples have been prepared by the heat treatment of a pressed mixture of Mg and MgB2 powders. It was found that linked superconducting structure is formed down to the minimum normalized density gamma= d/do= 0.16…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
This review paper illustrates the main normal and superconducting state properties of magnesium diboride, a material known since early 1950's, but recently discovered to be superconductive at a remarkably high critical temperature Tc=40K…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
The superconducting properties of copper-sheathed MgB2 wires fabricated by conventional powder-in-tube techniques and the in-situ reaction procedure are analysed. The influence of the processing conditions and initial (1+x)Mg + 2B (x = 0,…
Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in…
Superconducting Ag or Cu sheathed MgB2 wires have been fabricated by conventional powder-in-tube techniques. The in-situ reaction of Mg and B powders with atomic proportions of 1:2 and 1.33:2 inside Ag or Cu tubes at low temperatures have…
The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT…
In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
Far-infrared reflectivity studies on the polycrystalline intermetallic compound MgB_2 with a superconducting transition temperature T_c=39 K were performed at temperatures 20 K to 300 K. We observe a significant raise of the…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
The discovery of superconductivity at 39 K in magnesium diboride offers the possibility of a new class of low-cost, high-performance superconducting materials for magnets and electronic applications. With twice the critical temperature of…
Detailed magneto-transport data on dense wires of $MgB_2$ are reported for applied magnetic fields up to 18 T. The temperature and field dependencies of the electrical resistivity are consistent with $MgB_2$ behaving like a simple metal and…