We propose a theoretical model for branching instabilities in 2-dimensional fracture, offering predictions for when crack branching occurs, how multiple cracks develop, and what is the geometry of multiple branches. The model is based on…
On microscopic and mesoscopic scales, plastic flow of crystals is characterized by large intrinsic fluctuations. Deformation by crystallographic slip occurs in a sequence of intermittent bursts ('slip avalanches') with power-law size…
Crack advance from short or long pre-cracks is predicted by the progressive failure of a cohesive zone in a strain gradient, elasto-plastic solid. The presence of strain gradients leads to the existence of an elastic zone at the tip of a…
Recently the scaling laws describing the roughness development of fracture surfaces was proposed to be related to the macroscopic elastic energy released during crack propagation [Mor00]. On this basis, an energy-based asymptotic analysis…
Metals owe their unique mechanical properties to how defects emerge and propagate within their crystal structure under stress. However, the mechanisms leading from the early emerging (local) defects to the amplification of dislocations…
We discuss avalanche and finite size fluctuations in a mesoscopic model to describe the shear plasticity of amorphous materials. Plastic deformation is assumed to occur through series of local reorganizations. Yield stress criteria are…
Slow crack propagation in ductile, and in certain brittle materials, appears to take place via the nucleation of voids ahead of the crack tip due to plastic yields, followed by the coalescence of these voids. Post mortem analysis of the…
Unstable growth of cracks (rough crack surface and crack branching) in dynamic fracture has long been observed in various materials. Until now, there was no universally agreed upon explanation for these instabilities. Here, we demonstrate…
Fracture growth in a material is strongly influenced by the presence of inhomogeneities, which deviate crack trajectories from rectilinearity and deeply affect failure. Increasing crack tortuosity is connected to enhancement of fracture…
Fatigue fracture is one of the main causes of failure in structures. However, the simulation of fatigue crack growth is computationally demanding due to the large number of load cycles involved. Metals in the low cycle fatigue range often…
We introduce a class of models based on near crack tip degradation of materials that can account for fracture growth under cyclic loads below the Griffith threshold. We incorporate the gradual degradation due to a cyclic load through a flow…
Spontaneous brittle fracture is studied based on the recently introduced model (Mishuris and Slepyan, Brittle fracture in a periodic structure with internal potential energy. Proc. Roy. Soc. A, in press). A periodic structure is considered,…
Fatigue fracture in ductile materials, e. g. metals, is caused by cyclic plasticity. Especially regarding the high numbers of load cycles, plastic material models resolving the full loading path are computationally very demanding. Herein, a…
A continuum model of fracture that describes, in principle, the propagation and interaction of arbitrary distributions of cracks and voids with evolving topology without a fracture criterion is developed. It involves a 'law of motion' for…
For solving the longstanding materials science problem of correlating elastic properties of a solid material to the formation of cracks we present a new general concept. This concept is applied to the technologically most important cracks…
We discuss crack propagation along the interface between two dissimilar materials. The crack edge separates two states of the interface, ``stick'' and ``slip''. In the slip region we assume that the shear stress is proportional to the…
Linear Elastic Fracture Mechanics (LEFM) provides a consistent framework to evaluate quantitatively the energy flux released to the tip of a growing crack. Still, the way in which the crack selects its velocity in response to this energy…
We address analytically and numerically the problem of crack path prediction in the model system of a crack propagating under thermal loading. We show that one can explain the instability from a straight to a wavy crack propagation by using…
We examine theoretically and numerically fast propagation of a tensile crack along unidimensional strips with periodically evolving toughness. In such dynamic fracture regimes, crack front waves form and transport front disturbances along…
The slow motion of a crack line is studied via an experiment in which sheets of paper are split into two halves in a ``peel-in-nip'' (PIN) geometry under a constant load, in creep. The velocity-force relation is exponential. The dynamics of…