Crack fronts deform due to heterogeneities, and inspecting these deformations can reveal local variations of material properties, and help predict out of plane damage. Current models neglect the influence of a finite dissipation…
Crack front waves (FWs) are dynamic objects that propagate along moving crack fronts in 3D materials. We study FW dynamics in the framework of a 3D phase-field framework that features a rate-dependent fracture energy $\Gamma(v)$ ($v$ is the…
Fractures are a critical process in how materials wear, weaken, and fail whose unpredictable behavior can have dire consequences. While the behavior of smooth cracks in ideal materials is well understood, it is assumed that for real,…
Patterns on broken surfaces are well-known from everyday experience, but surprisingly, how and why they form are very much open questions. Well-defined facets are commonly observed1-4 along fracture surfaces which are created by slow…
Cracks, the major vehicle for material failure, tend to accelerate to high velocities in brittle materials. In three-dimensions, cracks generically undergo a micro-branching instability at about 40% of their sonic limiting velocity. Recent…
Crack growth is the basic mechanism leading to the failure of brittle materials. Engineering addresses this problem within the framework of continuum mechanics, which links deterministically the crack motion to the applied loading. Such an…
Cracks develop various surface patterns as they propagate in three-dimensional (3D) materials. Facet formation in nominally tensile (mode-I) fracture emerge in the slow, non-inertial regime and oftentimes takes the form of surface steps. We…
The dynamics of tensile crack fronts restricted to advance in a plane are studied. In an ideal linear elastic medium, a propagating mode along the crack front with a velocity slightly less than the Rayleigh wave velocity, is found to exist.…
Fracture behavior in architected materials can be influenced by heterogeneities, yet the mechanisms by which imperfections affect crack propagation remain poorly understood. In this study, we introduce well-controlled, localized defects in…
During brittle crack propagation, a smooth crack front curve frequently becomes disjoint, generating a stepped crack and a material ligament that unites the newly formed crack fronts. These universal features fundamentally alter the…
The pattern development of multiple cracks in extremely anisotropic solids such as bilayer or multilayer two-dimensional (2D) crystals contains rich physics, which, however, remains largely unexplored. We studied crack interaction across…
Fracture propagation is highly sensitive to the conditions at the crack tip. In heterogeneous materials, microscale obstacles can cause propagation instabilities. Macroscopic heterogeneities modify the stress field over scales larger than…
Strong interaction of closely located, nearly parallel hydraulic fractures and its influence on their propagation are studied. Both computational and physical aspects of the problem are considered. It is shown that from the computational…
Fracture is a fundamental mechanism of materials failure. Propagating cracks can exhibit a rich dynamical behavior controlled by a subtle interplay between microscopic failure processes in the crack tip region and macroscopic elasticity. We…
When a crack interacts with material heterogeneities, its front distorts and adopts complex tortuous configurations that are reminiscent of the energy barriers encountered during crack propagation. As such, the study of crack front…
The morphology of fracture surfaces encodes the various complex damage and fracture processes occurring at the microstructure scale that have lead to the failure of a given heterogeneous material. Understanding how to decipher this…
The failure of materials and interfaces is mediated by cracks, nearly singular dissipative structures that propagate at velocities approaching the speed of sound. Crack initiation and subsequent propagation -- the dynamic process of…
Mixed mode (I+III) loading induces segmented crack front \'echelon structures connected by steps. We study this instability in a highly deformable, strain-hardening material. We find that \'echelons develop beyond a finite, size-independent…
Understanding the role played by the microstructure of materials on their macroscopic failure properties is an important challenge in solid mechanics. Indeed, when a crack propagates at a heterogeneous brittle interface, the front is…
The dynamics and stability of brittle cracks are not yet fully understood. Here we use the Willis-Movchan 3D linear perturbation formalism [J. Mech. Phys. Solids {\bf 45}, 591 (1997)] to study the out-of-plane stability of planar crack…