Sb- and Se-substituted CeOBiS2 single crystals have been successfully grown using CsCl/KCl flux. Sb and Se substitution dependence of the superconductivity on CeOBiS2 was investigated and the superconducting phase diagram at above 0.3 K was…
"F-free" CeOBiS$_2$ single crystals have successfully grown, thoroughly eliminating a concern about F-contamination by using a high-purity CsCl flux. The obtained crystals have a plate-like shape with a size of 1.0-3.0 mm in the…
F-substituted ROBiS2 (R = La, Ce, Nd) superconducting single crystals with different F concentration were grown successfully using CsCl/KCl flux. All the obtained single crystals had a plate-like shape with a well-developed ab-plane of 1-2…
(La,Ce)OBiS2 single crystals are successfully grown using CsCl flux. The obtained single crystals have a plate-like shape with a size of 0.5-2.0 mm and a well-developed ab-plane. The thickness of the crystals increases with a decrease in…
Single crystals of Ce-doped (La,Pr)OBiS2 superconductors, multinary rare-earth elements substituted ROBiS2, were successfully grown. The grown crystals typically had a size of 1-2 mm and a plate-like shape with a well-developed c-plane. The…
We report the Se substitution effects on the crystal structure, superconducting properties, and valence states of self-doped BiCh2-based compound CeOBiS2-xSex. Polycrystalline CeOBiS2-xSex samples with x = 0-1.0 were synthesized. For x =…
F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of…
Resistivities of single-crystalline as well as poly-crystalline samples of CeOBiS2 without fluorine doping were measured at temperatures down to 0.13 K, and were compared with those of poly-crystalline LaOBiS2 and PrOBiS2. Both…
F-substituted LaOBiSe2 single crystals were grown using CsCl flux. The obtained single crystals showed a plate-like shape with a size of about 1.0 mm square. The c-axis lattice constant of the grown crystals was determined to be 14.114(3)…
PrOBiS2 single crystals were successfully grown using a KCl flux. The obtained crystals had a plate-like shape with a typical size of 0.5-1.0 mm and well-developed ab-plane. The Pr valence of the grown crystals, as determined by an X-ray…
Superconductivity is achieved in Nd1-xCexOBiS2 via electron doping using mixed-valence Ce ions. Single crystals with x = 0.2, 0.3, 0.4, and 0.5 are generated using a CsCl flux method. Plate-like single crystals with dimensions of 0.8 0.8…
Cd-doped La(O,F)BiS2 single crystals were grown using a CsCl/KCl flux. The grown crystals have a plate-like shape with ~1-2 mm square size in a well-developed ab-plane. The Cd doping in the crystals was successfully characterized by single…
Carbon-substituted MgB2 single crystals, Mg(B_1-xC_x)_2 of 0.3-1.0 mm size were grown for x=0.02-0.15 by a high-pressure technique. The doping dependence of lattice constants studied in a range of x=0.0-0.2 shows a monotonic decrease in a,…
We prepared a set of Pb-substituted Bi_{2-x}Pb_xSr_2ErCu_2O_8 single crystals. The resistivity and the in-plane thermopower decrease with increasing x from 0 to 0.8, which indicates that the Pb substitution supplies holes in the CuO_2…
We report the evolution of superconductivity and the phase diagram of the KxFe2-ySe2-zTez (z=0-0.6) crystals grown by a simple one-step synthesis. No structural transition is observed in any crystals, while lattice parameters exhibit a…
We have systematically investigated the crystal structure, magnetic susceptibility, and electrical resistivity of the BiS2-based superconductor LaO0.5F0.5Bi(S1-xSex)2 (x = 0 - 0.7). With expanding lattice volume by Se substitution, bulk…
Superconductivity was discovered in a Ni0:05TaS2 single crystal. A Ni0:05TaS2 single crystal was successfully grown via the NaCl/KCl flux method. The obtained lattice constant c of Ni0:05TaS2 is 1.1999 nm, which is significantly smaller…
Superconducting Sm(O,F)BiS2 single crystals were successfully grown using KI-KCl flux. The obtained single crystals were flat-shaped and their size was 500um. The structure and composition of the obtained single crystals were obtained using…
We report the effect of Se substitution on the crystal structure and superconductivity of BiCh2-based (Ch: S, Se) layered compounds Eu0.5Ce0.5FBiS2-xSex (x = 0-1). Crystal structure analysis showed that both lattice constants, a and c,…
Ce(O,F)Sb(S,Se)2 single crystals were successfully grown using a CsCl/KCl flux method. The obtained crystals have a plate-like shape with the typical size of 1-2 mm and well-developed ab-plane, which enables X-ray single crystal structural…