Related papers: Enhanced weak superconductivity in trigonal $\gamm…
We have determined the resistive upper critical field Hc2 for single crystals of the superconductor Fe1.11Te0.6Se0.4 using pulsed magnetic fields of up to 60T. A rather high zero-temperature upper critical field of mu0Hc2(0) approx 47T is…
The electrical resistivity \rho(T) and heat capacity C(T) on single crystals of SrNi2As2 and EuNi2As2 are reported. While there is no evidence for a structural transition in either compound, SrNi2As2 is found to be a bulk superconductor at…
We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
Magnetisation and magnetoresistance measurements have been carried out on superconducting Ba1-xKxFe2As2 samples with x=0.40 and 0.50. From low field magnetization data carried out at different temperatures below TC, HC1 has been extracted.…
We propose an analytical model devoted to explain the anisotropy of the electrical resistance observed below the critical temperature in granular high-Tc superconductors submitted to a magnetic field H. Reported experimental results…
We have investigated the temperature dependence of the resistive upper critical fields ($\mu_{0}H_{\rm c2}(T)$) for an Fe$_{1.05}$Te$_{0.85}$Se$_{0.15}$ single crystal, which exhibit superconductivity at $T_{\rm c} \sim 14 K, in magnetic…
Magnetoresistivity measurements with fine tuning of the field direction on high quality single crystals of the ferromagnetic superconductor UCoGe show anomalous anisotropy of the upper critical field H_c2. H_c2 for H // b-axis (H_c2^b) in…
We examine the superconducting anisotropy $\gamma_c = (m_c / m_{ab})^{1/2}$ of a metallic high-$T_c$ superconductor MgB$_2$ by measuring the magnetic torque of a single crystal. The anisotropy $\gamma_c$ does not depend sensitively on the…
We report resistivity and calorimetric measurements on two single crystals of CePd2Si2 pressurized up to 7.4 GPa. A weak uniaxial stress induced in the pressure cell demonstrates the sensitivity of the physics to anisotropy. Stress applied…
A superconducting transition in the temperature dependence of the ab-plane resistivity of underdoped YBa_2Cu_3O_{6+x} crystals in the range T_c<30 K has been investigated. Unlike the case of samples with the optimal level of doping, the…
The temperature dependence of the upper critical magnetic field (Hc2) in a BaFe1.84Co0.16As2 single crystal was determined via resistivity, for the inter-plane (H^ab) and in-plane (H//ab) directions in pulsed and static magnetic fields of…
We report measurements of electrical resistivity under pressure to 5.8 GPa, magnetization to 6.7 GPa,and ac susceptibility to 7.1 GPa in KFe2As2. The previously reported change of slope in the pressure dependence of the superconducting…
Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated…
We report resistivity measurements performed on KFe$_2$As$_2$ single crystals down to $T$ = 0.3 K and in magnetic fields up to 17.5 T. The in-plane resistivity vs. $T$ curve has a convex shape down to $\sim$50 K and shows a $T^2$ dependence…
Comprehensive low-temperature specific heat data C(T,H) of Na_0.35CoO2-1.3H_2O with temperature T down to 0.6 K and the magnetic field H up to 8 T are presented. For the normal state, the values of gamma_n=13.94 mJ/mol K2, and Debye…
Anisotropic superconducting properties including the upper critical field Hc2, thermal activation energy U0, and critical current density Jc are systematically studied in a large Ca1-xLaxFeAs2 single crystal (x ~ 0.18). The obtained Hc2…
The upper critical fields, $H_{c2}$($T$), of single crystals of the superconductor Ca$_{10}$(Pt$_{4-\delta}$As$_{8}$)((Fe$_{0.97}$Pt$_{0.03}$)$_{2}$As$_{2}$)$_{5}$ ($\delta$ $\approx$ 0.246) are determined over a wide range of temperatures…
The transport and magnetic studies are performed on high quality FeTe0.60Se0.40 single crystals to determine the upper critical fields (Hc2), lower critical field (Hc1) and the Critical current density (Jc). The value of upper critical…
The high upper critical field and low anisotropy of iron-based superconductors make them being particularly attractive for high-field applications. However, the current carrying capability needs to be enhanced by overcoming the weak-link…