In this paper for the first time we report the results of molecular dynamics simulation of electrode/electrolyte interface of Li-O2 cathode under potential close to experimental values in 1M dimethyl sulfoxide (DMSO) solution of LiPF6 salt.…
By means of Density Functional Theory calculations we evaluate several lithium carbonate - graphite interface models as a prototype of the Solid Electrolyte Interphase capping layer on graphite anodes in lithium-ion batteries. It is found…
Silicon offers great promise as a potential anode active material and the optimum alternative to lithium metal in all-solid-state lithium-ion batteries. However, its practical application is limited by severe volume expansion (~300%) during…
Silicon-containing lithium-ion batteries can exhibit capacity gain early in life, which makes forecasting future cell behavior difficult. We have observed these anomalous trends even in conditions where known mechanisms, such as overhang…
Analysis of lithiation and delithiation kinetics in pulse-laser-deposited crystalline thin-film silicon (Si) electrodes is presented. Data from open-circuit relaxation experiments are used in conjunction with a model based on Tafel kinetics…
Silicon is a promising anode material for next-generation lithium-ion batteries due to its exceptionally high specific capacity (3600 mAh g$^{-1}$), significantly exceeding that of conventional graphite. However, its practical application…
The Solid-Electrolyte Interphase, SEI, formed on a battery electrode has been a central area of research for decades. This thin, complex layer profoundly impacts the electrochemical deposition morphology and stability of the metal in…
Atomic interface engineering (AIE) is critical for advancing technologies in energy storage, catalysis, and microelectronics. In anode-less lithium metal batteries (ALLMBs), AIE is essential for controlling interfacial chemistry governing…
The incorporation of ceramics into polymers, forming solid composite electrolytes (SCEs) leads to enhanced electrical performance of all-solid-state lithium metal batteries. This is because the dispersed ceramics particles increase the…
Next-generation lithium-ion batteries with silicon anodes have positive characteristics due to higher energy densities compared to state-of-the-art graphite anodes. However, the large volume expansion of silicon anodes can cause high…
Silicon is one of the most promising anode materials for Lithium-ion batteries. Silicon endures volume changes upon cycling, which leads to subsequent pulverization and capacity fading. These drawbacks lead to a poor lifespan and hamper the…
The biggest challenge for the commercialization of layered structured nickel rich lithium transition metal oxide cathode is the capacity and voltage fading. Resolving this problem over the years follows an incremental progress. In this…
An appropriate description of the lithiation/delithiation dynamics in bi-phasic primary cathode particles of Li-ion batteries requires an accurate treatment of the conditions holding at the interface between the particle and the surrounding…
In this paper, SiO2 layers deposited on 4H-SiC and subjected to different post deposition annealing (PDA) in NO and N2O were studied to identify the key factors influencing the channel mobility and threshold voltage stability in 4H-SiC…
Dendrite formation during electrodeposition while charging lithium metal batteries compromises their safety. While high shear modulus solid-ion conductors (SICs) have been prioritized to resolve pressure-driven instabilities that lead to…
The solid electrolyte interphase (SEI) is regarded as the most complex but the least understood constituent in secondary batteries using liquid and solid electrolytes. The nanostructures of SEIs were recently reported to be equally…
Interfacial deposition stability between Li metal and a solid electrolyte (SE) is important in preventing interfacial contact loss, mechanical fracture, and dendrite growth in Li-metal solid-state batteries (SSB). In this work, we…
Future lithium-based batteries are expected to use solid electrolytes to achieve higher energy density and fast charge capabilities. The majority of solid electrolytes are thermodynamically unstable against layered oxide cathodes. Here, the…
It is shown that continuously occurring electrolyte-reduction reaction on freshly-exposed electrode surfaces during lithiation/delithiation cycles causes the lowering of cycling efficiency, and hence, capacity fade in well-cycled silicon…
Silver interlayers have been shown to enable smooth lithium deposition and cycling in anode-free solid-state batteries. Here, we report the atomic structure of the Ag and Li interface, showing that Li preferentially plates as FCC on both…