Related papers: Probabilistic Modeling of LCF Failure Times Using …
We investigate the scatter in the cycles to crack initiation for conventionally cast specimens of the superalloy RENE 80 in total strain controlled low cycle fatigue (LCF) tests at 850{\deg}C. The grains at the location of crack initiation…
An accurate risk assessment for fatigue damage is of vital importance for the design and service of today's turbomachinery components. We present an approach for quantifying the probability of crack initiation due to surface driven…
Fatigue life of components or test specimens often exhibit a significant scatter. Furthermore, size effects have a non-negligible influence on fatigue life of parts with different geometries. We present a new probabilistic model for…
The failure time of samples of heterogeneous materials (wood, fiberglass) is studied as a function of the applied stress. It is shown that in these materials the failure time is predicted with a good accuracy by a model of microcrack…
The failure of a component often is the result of a degradation process that originates with the formation of a crack. Fatigue describes the crack formation in the material under cyclic loading. Activation and deactivation operations of…
This work provides a numerical calculation of shape gradients of failure probabilities for mechanical components using a first discretize, then adjoint approach. While deterministic life prediction models for failure mechanisms are not…
We formulate the problem of probabilistic predictions of global failure in the simplest possible model based on site percolation and on one of the simplest model of time-dependent rupture, a hierarchical fiber bundle model. We show that…
For the fatigue life of thin-walled components, not only fatigue crack initiation, but also crack growth is decisive. The phase-field method for fracture is a powerful tool to simulate arbitrary crack phenomena. Recently, it has been…
Mechanical components that are exposed to cyclic mechanical loading fail at loads that are well below the ultimate tensile strength. This process is known as fatigue. The failure time, that is the time when a first crack forms, is highly…
The present work discusses the micro-mechanism of low cycle fatigue (LCF) crack growth in smooth bar specimens of Haynes 282. Two parametric approaches, i.e. crack tip opening angle (CTOA) and maximum tangential stress ({\theta}MTS) have…
In this work we propose a stochastic model for estimating the occurrence of crack initiations on the surface of metallic specimens in fatigue problems that can be applied to a general class of geometries. The stochastic model is based on…
Predicting potential risks associated with the fatigue of key structural components is crucial in engineering design. However, fatigue often involves entangled complexities of material microstructures and service conditions, making…
The rainflow counting algorithm for material fatigue is both simple to implement and extraordinarily successful for predicting material failure times. However, it neglects memory effects and time-ordering dependence, and therefore runs into…
A probabilistic risk assessment for low cycle fatigue (LCF) based on the so-called size effect has been applied on gas-turbine design in recent years. In contrast, notch support modeling for LCF which intends to consider the change in…
Fatigue fracture is one of the main causes of failure in structures. However, the simulation of fatigue crack growth is computationally demanding due to the large number of load cycles involved. Metals in the low cycle fatigue range often…
In recent years a local probabilistic model for low cycle fatigue (LCF) based on the statistical size effect has been developed and applied on engineering components. Here, the notch support extension based on the stress gradient effect is…
An accurate assessment for fatigue damage as a function of activation and deactivation cycles is vital for the design of many engineering parts. In this paper we extend the probabilistic and local approach to this problem proposed in [1,2]…
A simple micromechanical model of polycrystalline materials is proposed, which enables us to swiftly produce grain-boundary-stress distributions induced by the uniform external loading (in the elastic strain regime). Such statistical…
Stress corrosion cracking (SCC) is a form of failure in metals that is present mostly in systems where humidity contact and mechanical load play a key role. Therefore, prediction of the combined effect is desired. There are models based on…
The research reveals the existence of a constant characteristic time of preparatory micro-structural processes before the onset of macro-failure at various high loading rates of brittle and quasi-brittle materials. The presence of this…