Related papers: A coupled phase field formulation for modelling fa…
Predicting lithium-ion battery lifetime is one of the greatest unsolved problems in battery research right now. Recent years have witnessed a surge in lifetime prediction papers using physics-based, empirical, or data-driven models, most of…
This is the first quantitative analysis of mechanical reliability of all-solid state batteries. Mechanical degradation of the solid electrolyte (SE) is caused by intercalation-induced expansion of the electrode particles, within the…
The phase field approach to modeling fracture uses a diffuse damage field to represent a crack. This addresses the singularities that arise at the crack tip in computations with sharp interface models, mollifying some of the difficulties…
Silicon anodes promise high energy densities of next-generation lithium-ion batteries, but suffer from shorter cycle life. The accelerated capacity fade stems from the repeated fracture and healing of the solid-electrolyte interphase (SEI)…
We present a phase field model (PFM) for simulating complex crack patterns including crack propagation, branching and coalescence in rock. The phase field model is implemented in COMSOL and is based on the strain decomposition for the…
Understanding the nature of brittle failure in ferroelectric materials is essential, but difficult due to the complex interaction between mechanical and electrical concentrated fields near the crack tip. In this work, an extended…
Environmentally assisted cracking phenomena are widespread across the transport, defence, energy and construction sectors. However, predicting environmentally assisted fractures is a highly cross-disciplinary endeavour that requires…
Fracture growth in a material is strongly influenced by the presence of inhomogeneities, which deviate crack trajectories from rectilinearity and deeply affect failure. Increasing crack tortuosity is connected to enhancement of fracture…
Fatigue crack growth is decisive for the design of thin-walled structures such as fuselage shells of air planes. The cold rolling process, used to produce the aluminium sheets this structure is made of, leads to anisotropic mechanical…
The phase field paradigm, in combination with a suitable variational structure, has opened a path for using Griffith's energy balance to predict the fracture of solids. These so-called phase field fracture methods have gained significant…
The crack phase field model has been well established and validated for a variety of complex crack propagation patterns within a homogeneous medium under either tensile or shear loading. However, relatively less attention has been paid to…
The unified 3D phase-field model for the description of the lithium-ion cell as a whole is developed. The model takes into account the realistic distribution of particles in porous electrodes, percolative transport of ions, and the…
Parameterisation of coupled degradation mechanisms in lithium-ion batteries is a major challenge. Interactions between the mechanisms depend on usage conditions: C-rate, rest state-of-charge (SoC), depth-of-discharge (DoD) and temperature.…
This study presents a novel coupled mechano-electro-chemical formulation for predicting stress corrosion cracking (SCC) phenomena in steel structures using the phase field method. SCC is a complex damage process that arises from the…
We extend a phase-field/gradient damage formulation for cohesive fracture to the dynamic case. The model is characterized by a regularized fracture energy that is linear in the damage field, as well as non-polynomial degradation functions.…
In the context of calling for low carbon emissions, lithium-ion batteries (LIBs) have been widely concerned as a power source for electric vehicles, so the fundamental science behind their manufacturing has attracted much attention in…
The phase-field approach to fracture has been proven to be a mathematically sound and easy to implement method for computing crack propagation with arbitrary crack paths. Hereby crack growth is driven by energy minimization resulting in a…
We present a generalised phase field-based formulation for predicting fatigue crack growth in metals. The theoretical framework aims at covering a wide range of material behaviour. Different fatigue degradation functions are considered and…
In this work, we present crack propagation experiments evaluated by digital image correlation (DIC) for a carbon black filled ethylene propylene diene monomer rubber (EPDM) and numerical modeling with the help of variational phase-field…
Long-term durability is a major obstacle limiting the widespread use of lithium ion batteries (LIBs) in heavy-duty applications and others demanding extended lifetime. As one of the root causes of degradation and failure of battery…