Related papers: Phase-field modeling of brittle fracture in hetero…
This contribution presents a diffuse framework for modeling cracks in heterogeneous media. Interfaces are depicted by static phase-fields. This concept allows the use of non-conforming meshes. Another phase-field is used to describe the…
Variational phase-field models of brittle fracture are powerful tools for studying Griffith-type crack propagation in complex scenarios. However, as approximations of Griffith's theory-which does not incorporate a strength criterion-these…
In this contribution, a variational diffuse modeling framework for cracks in heterogeneous media is presented. A static order parameter smoothly bridges the discontinuity at material interfaces, while an evolving phase-field captures the…
We propose a variational phase-field model of fracture capable of accounting for arbitrary closed convex strength domains. Unlike traditional models based on Ambrosio and Tortorelli regularization, the phase-field variable does not affect…
Understanding the nature of brittle failure in ferroelectric materials is essential, but difficult due to the complex interaction between mechanical and electrical concentrated fields near the crack tip. In this work, an extended…
We propose a new direction-dependent model for the unilateral constraint involved in the phase field approach to fracture and also in the continuous damage mechanics models. The construction of this phase field model is informed by…
A novel variational framework to model the fatigue behavior of brittle materials based on a phase-field approach to fracture is presented. The standard regularized free energy functional is modified introducing a fatigue degradation…
This paper addresses the modeling of fracture in quasi-brittle materials using a phase-field approach to the description of crack topology. Within the computational mechanics community, several studies have treated the issue of modeling…
A consistent treatment of the coupling of surface energy and elasticity within the multi-phase- field framework is presented. The model accurately reproduces stress distribution in a number of analytically tractable, yet non-trivial, cases…
We argue that nucleation of brittle cracks in initially flawless soft elastic solids is preceded by a nonlinear elastic instability, which cannot be captured without accounting for geometrical precise description of finite elastic…
In recent years, various phase field models have been developed in variational methods to simulate the failure of brittle solids. However, there is a lack of objective evaluation of the existing results, and in particular, there are few…
We propose a novel variational phase-field model for fracture in anisotropic materials. The model is specifically designed to allow a more flexible calibration of crack nucleation than existing anisotropic fracture formulations, while…
The present work deals with the behavior of fiber bundle model under heterogeneous loading condition. The model is explored both in the mean-field limit as well as with local stress concentration. In the mean field limit, the failure…
The phase-field model for fracture, despite its popularity and ease of implementation comes with its set of computational challenges. They are the non-convex energy functional, variational inequality due to fracture irreversibility, the…
The problem of a crack impinging on an interface has been thoroughly investigated in the last three decades due to its important role in the mechanics and physics of solids. In this investigation, this problem is revisited in view of the…
While crack nucleation and propagation in the brittle or quasi-brittle regime can be predicted via variational or material-force-based phase field fracture models, these models often assume that the underlying elastic response of the…
Fractures are a critical process in how materials wear, weaken, and fail whose unpredictable behavior can have dire consequences. While the behavior of smooth cracks in ideal materials is well understood, it is assumed that for real,…
In the context of the Damage Mechanics Challenge, we adopt a phase-field model of brittle fracture to blindly predict the behavior up to failure of a notched three-point-bending specimen loaded under mixed-mode conditions. The beam is…
A mathematical continuum limit of the interaction energy of a random particle chain is shown to yield new insight into the effect of microscopic heterogeneities on macroscopic fracture laws in brittle materials. We derive a formula which…
The phase field fracture method has emerged as a promising computational tool for modelling a variety of problems including, since recently, hydrogen embrittlement and stress corrosion cracking. In this work, we demonstrate the potential of…