High-quality and sizable single crystals are crucial for studying the intrinsic properties of unconventional superconductors, which are lacking in the 1111 phase of the Fe-based superconductors. Here we report the successful growth of…
Millimeter sized single crystals of CaFe$_{1-x}$Co$_x$AsF were grown using a self-flux method. It is found that high-quality single crystals can be grown from three approaches with different initial raw materials. The chemical compositions…
We report a simple, reliable method to grow high quality BaFe$_{2-x}$Co$_x$As$_2$ single crystal samples without using any fluxing agent. The starting materials for the single crystal growth come from well-crystallized polycrystalline…
Measurements of the anisotropic properties of single crystals play a crucial role in probing the physics of new materials. Determining a growth protocol that yields suitable high-quality single crystals can be particularly challenging for…
Self-nucleation in CdZnTe crystal growth remains a significant challenge, despite numerous attempts to achieve large-grain single crystals by restricting multi-nucleation during growth process using the traveling heater method. In this…
Co-doped iron arsenic single crystal of BaFe1.87Co0.13As2 with dimension up to 20 x 10 x 2 mm3 were grown by a nucleation pole: an alumina stick served as nucleation center during growth. The high quality of crystalline was illustrated by…
Single crystals of SmFeAsO1-xFy of a size up to 120 micrometers have been grown from NaCl/KCl flux at a pressure of 30 kbar and temperature of 1350-1450 C using the cubic anvil high-pressure technique. The superconducting transition…
CuFeO$_2$ single crystals up to 50 mm in length and up to 10 mm in diameter were grown by the optical floating-zone method. Stoichiometric polycrystalline rods with a diameter of 6-12 mm were used as feed materials to produce crystals of…
Centimeter sized platelet single crystals of KFe2As2 were grown using a self-flux method. An encapsulation technique using commercial stainless steel container allowed the stable crystal growth lasting for more than 2 weeks. Ternary K-Fe-As…
Superconducting whisker like and bulk single crystals of PrFeAs(O,F) were grown at 3 GPa and 1500 C from NaAs flux using the cubic anvil high pressure and high temperature technique. The ribbon shaped whisker like crystals were 400-1300…
We report the optimized conditions for growing the high quality single crystals of candidate quantum spin-ice Pr2Hf2O7 using the optical floating-zone method. Large single crystals of Pr2Hf2O7 have been grown under different growth…
A new approach to grow FeSe1-xTex single crystals with optical zone-melting technique was successfully employed. Crystals with actual composition 0.4 < x < 1.0 all show high crystallinity with no phase separation. The ability to visually…
Millimeter-sized single crystals of LaFeAsO, LaFeAsO1-xFx, and LaFe1-xCoxAsO were grown in NaAs flux at ambient pressure. The detailed growth procedure and crystal characterizations are reported. The as-grown crystals have typical…
Single crystals of Ba0.6K0.4Fe2As2 with excellent quality have been successfully grown without fluxing agent through a simple one-step method for the first time. X-ray diffraction patterns demonstrate that the samples have high crystalline…
Incorporation of $\mathrm{Al_{y}Ga_{1-y}N}$ (AGN) semiconductors into high power electronics offers efficiency improvements in power transmission, generation, and use, if approaches to eliminate the defects arising from film-lattice…
A description is given of the traveling solvent technique, which has been used for the crystal growth of both congruently and incongruently melting materials of many classes of intermetallic, chalcogenide, semiconductor and oxide materials.…
We grew (Hg,Re)Ba$_2$Ca$_2$Cu$_3$O$_{8+\delta}$ ((Hg,Re)1223) single crystals with good reproducibility via the single-step flux method using monoxides as raw materials. A double-sealing method using a thick-walled quartz tube and a…
We have grown underdoped (x = 0.11, 0.12) and optimally doped (x = 0.16) La2-xSrxCuO4 (LSCO) crystals by traveling-solvent floating-zone (TSFZ) technique. In order to obtain LSCO single crystals of high quality, we have made much effort to…
MgO single crystals with diameters between 3.5 and 5 mm and lengths up to 40 mm were grown by the optical floating zone technique (OFZ). Despite challenging material properties such as the high melting point of 2825 {\deg}C, very high…
Single crystals of A$_{1-x}$K$_x$Fe$_2$As$_2$ (A=Ba, Sr) with high quality have been grown successfully by FeAs self-flux method. The samples have sizes up to 4 mm with flat and shiny surfaces. The X-ray diffraction patterns suggest that…