Related papers: Chemo-Mechanical Model of SEI Growth on Silicon El…

Cycle life is critically important in applications of rechargeable batteries, but lifetime prediction is mostly based on empirical trends, rather than mathematical models. In practical lithium-ion batteries, capacity fade occurs over…

The capacity fade of modern lithium ion batteries is mainly caused by the formation and growth of the solid-electrolyte interphase (SEI). Numerous continuum models support its understanding and mitigation by studying SEI growth during…

Mathematical models of capacity fade can reduce the time and cost of lithium-ion battery development and deployment, and growth of the solid-electrolyte interphase (SEI) is a major source of capacity fade. Experiments in Part I reveal…

Higher energy density and longer lifetime are the requirements for next-generation lithium-ion batteries. A promising anode material is silicon, which offers high specific capacity, but its significant volume change during lithiation and…

Accurately predicting aging of lithium-ion batteries would help to prolong their lifespan, but remains a challenge owing to the complexity and interrelation of different aging mechanisms. As a result, aging prediction often relies on…

Continued growth of the solid electrolyte interphase (SEI) is the major reason for capacity fade in modern lithium-ion batteries. This growth is made possible by a yet unidentified transport mechanism that limits the passivating ability of…

This work proposes a semi-empirical model for the SEI growth process during the early stages of lithium-ion battery formation cycling and aging. By combining a full-cell model which tracks half-cell equilibrium potentials, a…

Electrolyte reduction products form the solid-electrolyte interphase (SEI) on negative electrodes of lithium-ion batteries. Even though this process practically stabilizes the electrode-electrolyte interface, it results in continued…

Growth of the solid electrolyte interphase (SEI) is a primary driver of capacity fade in lithium-ion batteries. Despite its importance to this device and intense research interest, the fundamental mechanisms underpinning SEI growth remain…

Charge lost per unit surface area of a silicon electrode due to the formation of solid-electrolyte-interphase (SEI) layer during initial lithiation was quantified, and the species that constitute this layer were identified. Coin cells made…

The solid-electrolyte interphase (SEI) substantially influences the lifetime of lithium-ion batteries. Nevertheless, the transport mechanism responsible for the long-term growth of the SEI remains controversial. This study aims at…

Understanding solid liquid interfaces at high spatial and chemical resolution is crucial for advancing electrochemical energy storage technologies, yet this remains a persistent challenge due to the lack of characterisation techniques that…

Using cryogenic transmission electron microscopy, we revealed three dimensional (3D) structural details of the electrochemically plated lithium (Li) flakes and their solid electrolyte interphase (SEI), including the composite SEI skin-layer…

Next-generation lithium-ion batteries with silicon anodes have positive characteristics due to higher energy densities compared to state-of-the-art graphite anodes. However, the large volume expansion of silicon anodes can cause high…

During the first charge-discharge cycle, silicon-based batteries show an important capacity loss because of the formation of the solid electrolyte interphase (SEI) and morphological changes due to expansion-contraction sequence upon…

We present a coupled mechanistic approach that elucidates the intricate interplay between stress and electrochemistry, enabling the prediction of the onset of instabilities in Li-metal anodes and the solid electrolyte interphase (SEI) in…

Silicon is a promising anode material for next-generation lithium-ion batteries due to its exceptionally high specific capacity (3600 mAh g$^{-1}$), significantly exceeding that of conventional graphite. However, its practical application…

Silicon is a promising anode material for next-generation lithium-ion batteries. However, the volume change and the voltage hysteresis during lithiation and delithiation are two substantial drawbacks to their lifetime and performance. We…

Understanding the mechanical interplay between silicon anodes and their surrounding solid-electrolyte interphase (SEI) is essential to improve the next generation of lithium-ion batteries. We model and simulate a 2D elliptical silicon…

The path toward Li-ion batteries with higher energy-densities will likely involve use of thin lithium metal (Li) anode (<50 $\mu$m in thickness), whose cyclability today remains limited by dendrite formation and low Coulombic efficiency.…