Related papers: High-performance Ba1-xKxFe2As2 superconducting tap…

Superconducting joints are one of the key technologies to make Ba1-xKxFe2As2 (Ba-122) superconducting wires or tapes for high-field applications. Herein, superconducting joints were fabricated by a simple cold-pressing method, and the joint…

From the application point of view, large critical current densities Jc (H) for superconducting wires are required, preferably for magnetic fields higher than 5 T. Here we show that strong c-axis textured Sr1-xKxFe2As2 tapes with nearly…

We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…

We report the realization of grain alignment in Sn-added Sr1-xKxFe2As2 superconducting tapes prepared by ex-situ powder-in-tube method. At 4.2 K, high transport critical current densities Jc of 2.5x10^4 A/cm^2 (Ic = 180 A) in self-field and…

The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…

The recently discovered iron-based superconductors with very high upper critical field and small anisotropy have been regarded as a potential candidate material for high field applications. However, enhancements of superconducting…

The high upper critical field and low anisotropy of iron-based superconductors make them being particularly attractive for high-field applications. However, the current carrying capability needs to be enhanced by overcoming the weak-link…

Superconducting joints are essential for iron-based superconductor's applications in future. In this study, a process for fabricating superconducting joints between Sr1-xKxFe2As2 (Sr-122) tapes is developed for the first time. The Ag sheath…

High temperature (high-Tc) superconductors like cuprates have superior critical current properties in magnetic fields over other superconductors. However, superconducting wires for high-field-magnet applications are still dominated by…

The c-axis textured Sr1-xKxFe2As2 tapes produced by cold rolling and post-annealing, could carry a high super-current over 2*104 A/cm2. However, the magnitude is far from its maximum, because of the current obstacles associated with various…

122 type pnictide superconductors are of particular interest for high-field applications because of their large upper critical fields Hc2 (> 100 T), low Hc2 anisotropy r (< 2), and high thin-film critical current densities Jc (> 1 MA/cm2 at…

The K- and Co-doped BaFe2As2 (Ba-122) superconducting compounds are potentially useful for applications because they have upper critical fields (Hc2) of well over 50 T, Hc2 anisotropy Gamma < 2, and thin film critical current densities…

Thin films of the iron-based superconductor BaFe2(As1-xPx)2 (Ba122:P) were fabricated on polycrystalline metal-tape substrates with two kinds of in-plane grain boundary alignments (well aligned (4 deg.) and poorly aligned (8 deg.)) by…

Fe-clad BaxK1-xFe2As2 superconducting tapes were fabricated by the ex situ powder-in-tube method combined with a short high-temperature annealing technique. The effect of annealing time and different dopants on the transport properties of…

Ag-sheathed CaKFe4As4 superconducting tapes have been fabricated via the ex-situ powder-in-tube method. Thermal and X-ray diffraction analyses suggest that the CaKFe4As4 phase is unstable at high temperatures. It decomposes into the CaAgAs…

The paper reports the first successful fabrication of MgB2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The…

We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of…

The iron-based superconductor Ba$_{1-x}$K$_x$Fe$_\text{2}$As$_\text{2}$ is emerging as a key material for high magnetic field applications owing to the recent developments in superconducting wires and bulk permanent magnets. Epitaxial thin…

Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament…

Copper sheath is the first choice for manufacturing high-Tc superconducting wires and tapes because of its high electrical and thermal conductivities, low cost and good mechanical properties. However, Cu can easily react with…