In the present work the effect of surface roughness on oxidation behavior during the early stages of high temperature exposure of Ni-base superalloy IN 625 is described. The surface roughness was described using standard contact…
The effects of surface preparations on oxidation kinetics and oxide scale morphology for the commercially available Ni-based superalloy IN 713C have been investigated. The ground and polished samples were exposed in air at 800-1100C. The…
In the present paper, the analysis of polishing, grinding and sand-blasting processes on oxidation behavior of nickel, copper and nickel-copper alloy has been investigated. Surface roughness has been measured using two methods: by contact…
Fe based alloys are commonly used in almost every sector of human life. For different reasons, the surfaces of the real parts are prepared using different methods, e.g., mirror-like polishing, grit-blasting, etc. The purpose of the present…
In Ni-base superalloys with low Al and/or Ti content the precipitation and subsequent coarsening of gamma' particles at intermediate temperatures contribute to the degradation of the mechanical properties of the alloy. In the present paper…
The microstructural stability and mechanical properties of superalloys at high temperatures are significantly influenced by the composition and nature of the solutes they contain. Most of the alloys with high solvus temperature have higher…
There are still debates regarding the mechanisms that lead to hot cracking in parts build by additive manufacturing (AM) of non-weldable Ni-based superalloys. This lack of in-depth understanding of the root causes of hot cracking is an…
Ni-based structural alloys in molten salt environments often experience simultaneous mechanical loading and corrosive attack, yet the mechanisms governing stress-corrosion interactions remain unclear. Prior studies largely emphasize tensile…
The brittleness of an aluminide diffusion coating protecting a Ren\'e 125 Ni-based polycrystalline superalloy was investigated over a wide range of temperatures in its as-received and thermally aged form. Isothermal and thermal cycled aging…
We present an enhancement of spin properties of the shallow (<5nm) NV centers by using ALD to deposit titanium oxide layer on the diamond surface. With the oxide layer of an appropriate thickness, increases about 2 up to 3.5 times of both…
Cuprous oxide (Cu2O) films from 25 nm to 1500 nm were electrodeposited on n-Si(100) and Ni/n-Si(100) substrates from aqueous solution at room temperature. X-ray diffraction and transmission electron microscopy imaging show that the Cu2O…
A new class of crack-resistant nickel-based superalloy containing high $\gamma^\prime$ fraction is studied for the laser-powder bed fusion (L-PBF) process. The effects of the (Nb+Ta)/Al ratio is emphasised, a strategy that is shown to…
We experimentally discovered that Al2O3 and MgO exhibit well-pronounced nanometric modifications on the surfaces when irradiated under grazing incidence with 23 MeV I beam, in contrast to normal incidence irradiation with the same ion beam…
We investigate the impact of the oxidizing character of the nitric medium on the evolution of the intergranular corrosion of a stainless steel. In two different oxidizing conditions ("severe" and "soft"), the corroded surface of the steel…
Aluminum and their alloys, after careful treatments, can develop excellent mechanical, tribological, electrical and chemical (high corrosion resistance) properties. However, 7000 series, with Cu in the alloy, have a poor corrosion…
A single graphene layer placed between two parallel Ni(111) surfaces screens the strong attractive force and results in a significant reduction of adhesion and sliding friction. When two graphene layers are inserted, each graphene is…
The issue of ice accumulation at low-temperature circumstances causes multiple problems and serious damages in many civil infrastructures which substantially influence human daily life. However, despite the significant consideration in…
The service lives of nickel superalloys are often limited by environmental degradation. The present study compares oxidation, sulfidation and hot corrosion at 750C of three variants of a polycrystalline superalloy: a baseline alloy, a…
Surface-relief gratings fabricated through nanoimprint lithography (NIL) are prone to topographic distortion induced by resist shrinkage. Characterizing the impact of this effect on blazed diffraction efficiency is particularly important…
Surface roughness plays a critical role in ultrashort pulse laser ablation, particularly for industrial applications using burst mode operations, multi-pulse laser processing, and the generation of laser-induced periodic surface structures.…