Related papers: Interfacial Effects on Solid Electrolyte Interphas…
Solid electrolyte interphase (SEI), a thin layer that dynamically forms between active electrode and electrolyte during battery operation, critically governs the performance of rechargeable batteries1-5. An ideal SEI is expected to be…
In rechargeable batteries, electron transport properties of inorganics in the solid-electrolyte interphase (SEI) critically determine the safety, lifespan and capacity loss of batteries. However, the electron transport properties of…
Lithium ion batteries (LIB) can feature reactive anodes that operate at low potentials, such as lithium metal or silicon, passivated by solid electrolyte interphase (SEI) films. SEI is known to evolve over time as cycling proceeds. In this…
Electrolyte reduction products form the solid-electrolyte interphase (SEI) on negative electrodes of lithium-ion batteries. Even though this process practically stabilizes the electrode-electrolyte interface, it results in continued…
The development of next-generation electrochemical energy storage requires devices that combine the high energy density of batteries with the power capability and long cycle life of supercapacitors. However, the interfacial phenomena…
The Solid-Electrolyte Interphase, SEI, formed on a battery electrode has been a central area of research for decades. This thin, complex layer profoundly impacts the electrochemical deposition morphology and stability of the metal in…
Charging a Li ion battery requires Li ion transport between the cathode and the anode. This Li ion transport is dependent upon (among other factors) the electrostatic environment the ion encounters within the Solid Electrolyte Interphase…
In today's modeling and analysis of electrochemical cycling of Li- and Na-ion batteries, an assumption is often made regarding the interphase that forms between the active material and liquid electrolyte at low potentials, the so-called…
The solid electrolyte interphase (SEI) is regarded as the most complex but the least understood constituent in secondary batteries using liquid and solid electrolytes. The nanostructures of SEIs were recently reported to be equally…
The path toward Li-ion batteries with higher energy-densities will likely involve use of thin lithium metal (Li) anode (<50 $\mu$m in thickness), whose cyclability today remains limited by dendrite formation and low Coulombic efficiency.…
Continued growth of the solid electrolyte interphase (SEI) is the major reason for capacity fade in modern lithium-ion batteries. This growth is made possible by a yet unidentified transport mechanism that limits the passivating ability of…
Interfacial deposition stability between Li metal and a solid electrolyte (SE) is important in preventing interfacial contact loss, mechanical fracture, and dendrite growth in Li-metal solid-state batteries (SSB). In this work, we…
Battery interfaces help govern rate capability, safety/stability, cycle life, and self-discharge, but significant gaps remain in our understanding at atomic length scales that can be exploited to improve interfacial properties. In…
Nonaqueous aluminum-ion batteries are an interesting emerging energy storage technology, offering a plethora of advantages over existing grid energy storage solutions. Carbonaceous and graphitic materials are an appealing cathode material…
Fluoroethylene carbonate (FEC) shows promise as an electrolyte additive for improving passivating solid-electrolyte interphase (SEI) films on silicon anodes used in lithium ion batteries (LIB). We apply density functional theory (DFT), ab…
A rechargeable lithium metal battery (LMB), which uses metallic lithium at the anode, is among the most promising technologies for next generation electrochemical energy storage devices due to its high energy density, particularly when Li…
The solid electrolyte interphase SEI critically dictates the cyclability and Coulombic efficiency of sodium-metal batteries, yet its dynamic formation mechanisms and atomic-scale evolution during electrochemical cycling remain elusive due…
The capacity fade of modern lithium ion batteries is mainly caused by the formation and growth of the solid-electrolyte interphase (SEI). Numerous continuum models support its understanding and mitigation by studying SEI growth during…
Charge lost per unit surface area of a silicon electrode due to the formation of solid-electrolyte-interphase (SEI) layer during initial lithiation was quantified, and the species that constitute this layer were identified. Coin cells made…
Understanding and controlling the atomistic-level reactions governing the formation of the solid-electrolyte interphase (SEI) is crucial for the viability of next-generation solid state batteries. However, challenges persist due to…